PEI

PEI EXTEM™ XH1015-1000 SABIC INNOVATIVE US

226

Unit Price:US$ 23,375 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜transparent｜wear resistant
Application Areas:Electronic and electrical components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	4.2 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	120 Mpa
Bending modulus		ISO 178	2870 Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	3130 Mpa
Tensile strain	Break	ISO 527-2/5	7.0 %
elongation	Break	ASTM D638	10 %
Tensile strain	Yield	ISO 527-2/5	6.0 %
elongation	Yield	ASTM D638	7.0 %
tensile strength	Break	ISO 527-2/5	74.0 Mpa
	tensile strength	Break	ASTM D638	96.0 Mpa
	tensile strength	tensile strength	Yield	ISO 527-2/5	101 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	168 Mpa
Tensile modulus		ASTM D638	3420 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	3100 Mpa
tensile strength	Yield	ASTM D638	103 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：23to150°C	ISO 11359-2	5.1E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to150°C	ISO 11359-2	5E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	248 °C
	Vicat softening temperature	--	ISO 306/B50	250 °C
	Vicat softening temperature	Vicat softening temperature		ASTM D152510	260 °C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	224 °C
	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	237 °C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	235 °C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	250 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：3.20mm	Internal Method	1.0-1.2 %
Water absorption rate	23°C,24hr	ASTM D570	0.60 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	2.3 %
Melt Volume Flow Rate (MVR)	220°C/5.0kg	ISO 1133	0.00 cm3/10min
melt mass-flow rate	367°C/6.6kg	ASTM D1238	10 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PEI EXTEM™ XH1015-1000 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet