PPO NORYL™ SE1X-701 SABIC INNOVATIVE NANSHA
270
- Unit Price:US$ 4,836 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:35MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High temperature resistance｜Hydrolysis resistance
- Application Areas:Electronic and electrical components｜Mechanical component cover｜Household products
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 126 °C |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 117 °C | |
| RTI Elec | UL 746 | 110 °C | |
| RTI Imp | UL 746 | 105 °C | |
| RTI | UL 746 | 110 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-1 |
| 6.0 mm | UL 94 | V-0 | |
| Radiation board grade | RP100 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | -30°C, Energy at Peak | ASTM D3763 | 32.0 J |
| 23°C, Energy at Peak | ASTM D3763 | 51.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.50 - 0.70 % |
| 横向流动 2 | 内部方法 | 0.50 - 0.70 % | |
| Water absorption rate | 24 hr | ASTM D570 | 0.060 % |
| Outdoor applicability | UL 746C | f1 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | > 1.0E+15 ohms | |
| volume resistivity | ASTM D257 | 2.3E+16 ohms·cm | |
| dielectric strength | 3.20 mm, in Oil | ASTM D149 | 18 KV/mm |
| dielectric constant | 60 Hz | ASTM D150 | 2.52 |
| 50 kHz | ASTM D150 | 2.52 | |
| 1 MHz | ASTM D150 | 2.46 | |
| Dissipation Factor | 50 Hz | ASTM D150 | 3.4E-3 |
| 60 Hz | ASTM D150 | 3.4E-3 | |
| 1 MHz | ASTM D150 | 2.1E-3 | |
| arc resistance | ASTM D495 | PLC 6 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 1 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 105 to 110 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 30 to 70 % | ||
| Temperature at the rear of the barrel | 250 to 300 °C | ||
| Temperature in the middle of the barrel | 260 to 305 °C | ||
| Temperature at the front of the material cylinder | 270 to 310 °C | ||
| Spray nozzle temperature | 280 to 310 °C | ||
| Processing (melt) temperature | 280 to 310 °C | ||
| mold temperature | 75 to 105 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 20 to 100 rpm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 屈服 | ASTM D638 | 67.0 Mpa |
| 断裂 | ASTM D638 | 53.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 8.1 % |
| 断裂 | ASTM D638 | 20 % | |
| flexural modulus | 100 mm 跨距 | ASTM D790 | 2500 Mpa |
| bending strength | 屈服, 100 mm 跨距 | ASTM D790 | 102 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.