PC LUX9130T-NAT SABIC INNOVATIVE NANSHA

Unit Price:US$ 7,140 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Shenzhen Jiuhe New Material Technology Co., Ltd.

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:Plastic bag｜Lighting applications
Color:--
Grade:Halogen-free flame retardant grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	1000 μm	Internal Method	> 90.5	%
	transmissivity	2000 μm	Internal Method	> 90.0	%
		transmissivity	3000 μm	Internal Method	> 89.5	%
		transmissivity	transmissivity	6000 μm	ASTM D1003	> 88.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ASTM D4812	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ASTM D4812	无断裂
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	9.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0	kJ/m²
Dart impact	23°C, Total Energy	ASTM D3763	55.0	J
Suspended wall beam without notch impact strength	23°C7	ISO 180/1U	130	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C7	ISO 180/1U	130	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.40 mm	UL 94	V-2
	UL flame retardant rating	1.5 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	6.0 mm	UL 94	5VA
Burning wire flammability index	1.5 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	850	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--2	ASTM D638	2370	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2400	Mpa
tensile strength	Yield3	ASTM D638	64.0	Mpa
	tensile strength	Yield	ISO 527-2/50	64.0	Mpa
		tensile strength	Break3	ASTM D638	59.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	50.0	Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	98.0	Mpa
Bending modulus	--5	ISO 178	2410	Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2300	Mpa
elongation	Break	ISO 527-2/50	52	%
	elongation	Break3	ASTM D638	72	%
		elongation	Yield	ISO 527-2/50	6.0	%
		elongation	elongation	Yield3	ASTM D638	6.0	%
injection	Test Condition	Test Method	Test Result	Test Unit
Back pressure			0.300 to 0.700	Mpa
Screw speed			40 to 70	rpm
Exhaust hole depth			0.025 to 0.076	mm
Temperature at the rear of the barrel			265 to 290	°C
Temperature in the middle of the barrel			275 to 300	°C
drying temperature			120	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Suggested injection volume			40 to 60	%
Temperature at the front of the material cylinder			290 to 310	°C
Spray nozzle temperature			280 to 305	°C
Processing (melt) temperature			290 to 310	°C
Mold temperature			70 to 95	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.4E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.1E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.1E-5	cm/cm/°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	120	°C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span8	ISO 75-2/Be	131	°C
	Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	131	°C
Vicat softening temperature	--	ISO 306/B120	139	°C
Vicat softening temperature	Vicat softening temperature	--	ASTM D15259	137	°C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span8	ISO 75-2/Ae	120	°C
Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	8.0E-5	cm/cm/°C
RTI Elec		UL 746	115	°C
RTI Imp		UL 746	115	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	18	g/10 min
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	17.0	cm3/10min
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.45 - 0.65	%
Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.50 - 0.70	%
Water absorption rate	Saturation, 23°C	ISO 62	0.10	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.010	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	1.10 GHz	ASTM ES7-83	2.81
Dissipation factor	1.10 GHz	ASTM ES7-83	5.8E-3
Compared to the anti leakage trace index		UL 746	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 6530 /MT
Dongguan Xinda	US$ 7140 /MT

Supplier Join

Get App

Top

PC LUX9130T-NAT SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index