Material Properties:High impact resistance｜Thermal stability｜Filler: Glass fiber reinforced material｜45% filler by weight
Application Areas:Electrical applications｜small home appliances
Color:--
Grade:Enhanced level

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	218 °C
melting temperature		ISO 11357-3	221 °C

flammability	Test Condition	Test Method	Test Result
burning rate	1.00mm	ISO 3795	44 mm/min
FMVSS flammability		FMVSS302	B

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100 kJ/m²

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	TD	ISO 294-4	0.90 %
shrinkage rate	shrinkage rate	MD	ISO 294-4	0.10 %
Water absorption rate	饱和,23°C,2.00mm	ISO 62	4.9 %
Water absorption rate	Water absorption rate	平衡,23°C,2.00mm,50%RH	ISO 62	1.5 %
Ejection Temperature			210 °C
SpecificHeatCapacity of Melt			2100 J/kg/°C
ThermalConductivityofMelt			0.26 W/m/K
MediumDensity			1.33 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 1

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	14200 Mpa
tensile strength	断裂	ISO 527-2	215 Mpa
Tensile strain	断裂	ISO 527-2	3.0 %
Tensile creep modulus	1hr	ISO 899-1	-- Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	-- Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.