ABS STAREX® GC-0700 BK Samsung Cheil South Korea

198

Unit Price:US$ 1,580 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
100MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:transparent｜High temperature resistance
Application Areas:Special material for bottle caps｜Automotive components
Color:--
Grade:Heat resistant grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	40	kJ/m²
	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	200	J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	390	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.0mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	49.0	Mpa
bending strength	bending strength		ASTM D790	49.0	Mpa
Bending modulus		ISO 178	1760	Mpa
Bending modulus	Bending modulus		ASTM D790	1700	Mpa
Tensile strain	Break	ISO 527-2/50	11	%
elongation	Break	ASTM D638	17	%
tensile strength	Break	ISO 527-2/50	31.0	Mpa
	tensile strength	Break	ASTM D638	26.0	Mpa
		tensile strength	Yield	ISO 527-2/50	43.0	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	43.0	Mpa
Tensile modulus		ISO 527-2/50	2000	Mpa
Tensile modulus	Tensile modulus		ASTM D638	1800	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	80.0	°C
	Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	97.0	°C
		Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	85.0	°C
			Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	95.0	°C
				Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	73.0	°C
				Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	89.0	°C
Vicat softening temperature	--	ISO 306/B50	90.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	94.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD：3.20mm	ASTM D955	0.40-0.70	%
melt mass-flow rate	250°C/10.0kg	ISO 1133	40	g/10min
melt mass-flow rate	melt mass-flow rate	250°C/10.0kg	ASTM D1238	40	g/10min
density		ISO 1183	1.09	g/cm³
density	density		ASTM D792	1.09	g/cm³
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ISO 2039-2	95
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	95

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top