PA46 Stanyl® TW250F6 BK DSM JAPAN

230

Unit Price:US$ 5,744 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
95.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Flame retardant
Application Areas:Automotive Applications｜Electronic and electrical components
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	11 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-40°C	ISO 180/1A	11 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	60 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	50 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	11 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10 kJ/m²

flammability	Test Condition	Test Method	Test Result
Flammability level		UL 94	V-0
Flammability level	Flammability level		UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	160°C	ISO 178	5000 Mpa
	Bending modulus	120°C	ISO 178	6500 Mpa
	Bending modulus	Bending modulus	--	ISO 178	11000 Mpa
Tensile strain	Break, 160°C	ISO 527-2	4.0 %
	Tensile strain	Break, 120°C	ISO 527-2	4.0 %
	Tensile strain	Tensile strain	Break	ISO 527-2	2.5 %
tensile strength	Break, 160°C	ISO 527-2	95.0 Mpa
	tensile strength	Break, 120°C	ISO 527-2	105 Mpa
	tensile strength	tensile strength	Break	ISO 527-2	180 Mpa
Tensile modulus	160°C	ISO 527-2	6200 Mpa
	Tensile modulus	120°C	ISO 527-2	7500 Mpa
	Tensile modulus	Tensile modulus	--	ISO 527-2	12000 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI Elec	0.75 mm	UL 746	140 °C
Thermal Index - 5000 hr		IEC 60216	177 °C
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	5.5E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.5E-5 cm/cm/°C
Melting temperature		ISO 11357-3	295 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	290 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	290 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.68 g/cm³
Shrinkage rate	横向Flow	ISO 294-4	1.1 %
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.40 %
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.6 %

Electrical performance	Test Method	Test Result
Volume resistivity	IEC 60093	1.0E+14 ohms·cm
Dielectric strength	IEC 60243-1	30 KV/mm
Compared to the anti leakage trace index	IEC 60112	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.