Material Description
- Material Properties:Processability｜Moderate liquidity｜Ductility｜copolymer｜Good demolding performance
- Application Areas:Electrical applications｜Home appliance components｜Bottle cap
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 89 | |
| ASTM D785 | 121 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ASTM D648 | 124 °C | |
| ASTM D648 | 139 °C | ||
| ISO 75-2/Be | 140 °C | ||
| ISO 75-2/Ae | 128 °C | ||
| vicat | ASTM D152510 | 145 °C | |
| ISO 306/B50 | 145 °C | ||
| RTI Imp | UL 746 | 120 °C | |
| RTI Str | UL 746 | 125 °C | |
| RTI Elec | UL 746 | 130 °C | |
| Linear coefficient of thermal expansion | ASTME831 | 7.5E-05 cm/cm/°C | |
| ISO 11359-2 | 7.2E-05 cm/cm/°C | ||
| ISO 11359-2 | 7.2E-05 cm/cm/°C | ||
| ASTME831 | 7E-05 cm/cm/°C | ||
| vicat | ISO 306/B120 | 146 °C | |
| ball-indentation hardness | IEC 60695-10-2 | Pass |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 875 °C | |
| IEC 60695-2-13 | 875 °C | ||
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| IEC 60695-2-12 | 850 °C | ||
| UL flame retardant rating | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ISO 180/1U | NoBreak | |
| ISO 180/1U | NoBreak | ||
| Dart impact | ASTM D3763 | 70.0 J | |
| Impact strength of cantilever beam gap | ISO 180/1A | 60 kJ/m² | |
| ISO 180/1A | 70 kJ/m² | ||
| ASTM D256 | 870 J/m | ||
| ASTM D256 | 770 J/m | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak | |
| ISO 179/1eU | NoBreak | ||
| Charpy Notched Impact Strength | ISO 179/1eA | 65 kJ/m² | |
| ISO 179/1eA | 70 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | ASTM D150 | 9.3E-03 | |
| dielectric constant | ASTM D150 | 2.64 | |
| Dissipation Factor | ASTM D150 | 1.2E-03 | |
| dielectric strength | ASTM D149 | 16 KV/mm | |
| dielectric constant | ASTM D150 | 2.68 | |
| volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ISO 62 | 0.15 % | |
| ISO 62 | 0.35 % | ||
| shrinkage rate | 内部方法 | 0.40-0.80 % | |
| 内部方法 | 0.40-0.80 % | ||
| Melt volume flow rate | ISO 1133 | 9.00 cm3/10min | |
| melt mass-flow rate | ASTM D1238 | 10 g/10min | |
| density | ISO 1183 | 1.19 g/cm³ | |
| ASTM D792 | 1.18 g/cm³ |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 85.0 Mpa | |
| flexural modulus | ISO 178 | 2250 Mpa | |
| ASTM D790 | 2230 Mpa | ||
| Tensile strain | ISO 527-2/50 | 120 % | |
| elongation | ASTM D638 | 98 % | |
| Tensile strain | ISO 527-2/50 | 6.0 % | |
| tensile strength | ISO 527-2/50 | 60.0 Mpa | |
| elongation | ASTM D638 | 6.0 % | |
| tensile strength | ASTM D638 | 50.3 Mpa | |
| ISO 527-2/50 | 57.0 Mpa | ||
| ASTM D638 | 55.5 Mpa | ||
| Tensile modulus | ISO 527-2/1 | 2150 Mpa | |
| ASTM D638 | 2020 Mpa | ||
| bending strength | ASTM D790 | 92.4 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.