ABS XK-404 LG CHEM KOREA

391

Unit Price:US$ 3,240 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
18.5MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
ABS POLYLAC® D-2300 ZHENJIANG CHIMEI

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Hydrolysis resistance｜High temperature resistance
Application Areas:Power tool accessories｜Shell｜Electrical/Electronic Applications｜Automotive External Parts｜Automotive interior parts
Color:--
Grade:Heat resistant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	6.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	12	kJ/m²
Impact strength of cantilever beam gap	-30°C,3.20mm	ASTM D256	59	J/m
	Impact strength of cantilever beam gap	-30°C,6.40mm	ASTM D256	49	J/m
		Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	160	J/m
			Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	140	J/m
				Impact strength of cantilever beam gap	-30°C	ISO 180/1A	6.0	kJ/m²
				Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	13	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	3.20mm	ASTM D790	84.3	Mpa
Bending modulus		ISO 178	2550	Mpa
Bending modulus	Bending modulus	3.20mm	ASTM D790	2650	Mpa
elongation	Break,3.20mm	ASTM D638	20	%
tensile strength	Yield	ISO 527-2/50	54.0	Mpa
tensile strength	tensile strength	Yield,3.20mm	ASTM D638	52.0	Mpa
Tensile modulus		ISO 527-2/1	2450	Mpa
bending strength		ISO 178	82.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ASTM D15256	112	°C
Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/Ae	93.0	°C
	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	102	°C
		Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/Be	101	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	111	°C
RTI Str		UL 746	60.0	°C
RTI Imp		UL 746	60.0	°C
Vicat softening temperature		ISO 306/B50	112	°C
Linear coefficient of thermal expansion	MD：23to60°C	ISO 11359-2	8.0E-5to9.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to60°C	ISO 11359-2	8.0E-5to9.0E-5	cm/cm/°C
RTI Elec		UL 746	60.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220°C/10.0kg	ASTM D1238	7.0	g/10min
density		ISO 1183	1.05	g/cm³
density	density		ASTM D792	1.05	g/cm³
Shrinkage rate	MD：3.20mm	ISO 294-4	0.40-0.70	%
Shrinkage rate	Shrinkage rate	MD：3.20mm	ASTM D955	0.40-0.70	%
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	7.00	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Arc resistance		ASTM D495	PLC6
Dielectric strength	23°C,1.00mm	ASTM D149	33	KV/mm
Volume resistivity	23°C	ASTM D257	1.5E+03	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ISO 2039-2	114
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	112

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

ABS XK-404 LG CHEM KOREA

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index