LCP SUMIKASUPER® E6008MR SUMITOMO JAPAN

501

Unit Price:US$ 8,490 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
28MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜high strength
Application Areas:Household appliances｜Household appliances｜Automotive sector
Color:--
Grade:Extrusion grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	6.40 mm	ASTM D256	410	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.30 mm	UL 94	V-0
Extreme Oxygen Index		ISO 527-1	48	%
Solder resistance		Internal Method	300	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Poisson's ratio		ASTM D785	0.46
shear strength		ASTM D732	51.0	Mpa
bending strength	200°C	ASTM D790	33.0	Mpa
bending strength	bending strength	23°C	ASTM D790	143	Mpa
Bending modulus	200°C	ASTM D790	4900	Mpa
Bending modulus	Bending modulus	23°C	ASTM D790	12300	Mpa
elongation	Break	ASTM D638	5.2	%
tensile strength		ASTM D638	147	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			130	°C
drying time			4.0 to 24	hr
Temperature at the rear of the barrel			280 to 320	°C
Temperature in the middle of the barrel			320 to 350	°C
Temperature at the front of the material cylinder			340 to 370	°C
Spray nozzle temperature			340 to 370	°C
Processing (melt) temperature			360	°C
Mold temperature			40 to 160	°C
Injection pressure			80.0 to 160	Mpa
Injection speed			中等偏快
Maintain pressure			20.0 to 40.0	Mpa
Back pressure			1.00 to 5.00	Mpa
Screw speed			50 to 100	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
thermal conductivity		JIS R2618	0.52	W/m/K
Linear coefficient of thermal expansion	Across Flow : 150°C	Internal Method	5.6E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : 150°C	Internal Method	1.3E-5	cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	279	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Saturation	ASTM D570	0.020	%
Shrinkage rate	Flow	Internal Method	0.18	%
Shrinkage rate	Shrinkage rate	横向Flow	Internal Method	1.2	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112	PLC 4
Arc resistance		ASTM D495	130	sec
Dissipation factor	1 MHz	ASTM D150	0.022
Dissipation factor	Dissipation factor	1 kHz	ASTM D150	0.022
Dielectric constant	1 MHz	ASTM D150	3.90
Dielectric constant	Dielectric constant	1 kHz	ASTM D150	4.40
Volume resistivity		ASTM D257	1.0E+15	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	103

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.