Technical Data Sheet Compare

other	Test Condition	Test Method	Test Result
Color			白黑.透明

Basic performance	Test Condition	Test Method	Test Result
Water absorption rate		ASTM D-570	0.3 %

Mechanical properties	Test Condition	Test Method	Test Result
tensile strength		ASTM D-638	490 kg/cm
Rockwell hardness		ASTM D-785	115 R
bending strength		ASTM D-790	780 kg/cm
elongation at break		ASTM D-638	380 kg/cm
tensile strength		ASTM D638/ISO 527	490（屈服）380（断裂） kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	3.5 %
Rockwell hardness		ASTM D785	R-115
Flexural modulus		ASTM D790/ISO 178	23500 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	780 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap		ASTM D256/ISO 179	13 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	6 kg·cm/cm(J/M)ft·lb/in
elongation at break		ASTM D638/ISO 527	30 %

Other performance	Test Condition	Test Method	Test Result
melt viscosity		×10	插入式粘度计

Physical properties	Test Method	Test Result
density	ASTM D792/ISO 1183	1.08
Water absorption rate	ASTM D570/ISO 62	0.3 %
melt mass-flow rate	ASTM D1238/ISO 1133	19-23 g/10min

Thermal performance	Test Method	Test Result
combustibility	UL-94
Hot deformation temperature (HDT)	ASTM D-648	89 ℃
Combustibility (rate)	UL 94	HB
Hot deformation temperature (HDT)	ASTM D648/ISO 75	89 ℃（℉）
Linear expansion coefficient	ASTM D696/ISO 11359	1.2x10^-4 mm/mm.℃

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.