PC LEXAN™ 1414T SABIC INNOVATIVE SHANGHAI

244

Unit Price:US$ 4,667 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low temperature resistance｜transparent｜Easy to process｜Middle flow
Application Areas:Household appliances｜Bottle cap｜Electronic field｜Electrical field
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	70 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	60 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	23°C	ISO 179/1eA	70 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	65 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak
Dart impact	23°C,TotalEnergy	ASTM D3763	70.0 J

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield,50.0mmSpan	ASTM D790	92.4 Mpa
bending strength	bending strength		ISO 178	85.0 Mpa
Bending modulus		ISO 178	2250 Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	2230 Mpa
Tensile strain	Break	ISO 527-2/50	120 %
elongation	Break	ASTM D638	98 %
Tensile strain	Yield	ISO 527-2/50	6.0 %
elongation	Yield	ASTM D638	6.0 %
tensile strength	Break	ISO 527-2/50	60.0 Mpa
	tensile strength	Break	ASTM D638	50.3 Mpa
		tensile strength	Yield	ISO 527-2/50	57.0 Mpa
		tensile strength	tensile strength	Yield	ASTM D638	55.5 Mpa
Tensile modulus		ISO 527-2/1	2150 Mpa
Tensile modulus	Tensile modulus		ASTM D638	2020 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	139 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	124 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	128 °C
Vicat softening temperature		ASTM D152510	145 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	145 °C
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	7.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to80°C	ISO 11359-2	7.2E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	146 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to80°C	ISO 11359-2	7.2E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：3.20mm	Internal Method	0.40-0.80 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	9.00 cm3/10min
melt mass-flow rate	300°C/1.2kg	ASTM D1238	10 g/10min
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.35 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LEXAN™ 1414T SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet