PEI ULTEM™ 2300R-7301 SABIC INNOVATIVE US

273

Unit Price:US$ 24,709 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Flame retardant｜enhance
Application Areas:Automotive Applications｜Fitness equipment
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	3.20mm	ASTM D256	490 J/m

flammability	Test Condition	Test Method	Test Result
Extreme Oxygen Index		ASTM D2863	50 %
UL flame retardant rating	1.2mm	UL 94	5VA
UL flame retardant rating	UL flame retardant rating	0.25mm	UL 94	V-0
NBSSmokeDensity-Flaming,Ds,4min		ASTME662	1.60

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Break,100mmSpan	ASTM D790	228 Mpa
Bending modulus	100mmSpan	ASTM D790	8960 Mpa
elongation	Break	ASTM D638	3.0 %
tensile strength	Break	ASTM D638	159 Mpa
tensile strength	tensile strength	Yield	ASTM D638	169 Mpa
Tensile modulus		ASTM D638	9310 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ASTM D15255	228 °C
Linear coefficient of thermal expansion	MD：-20to150°C	ASTME831	2E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	210 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	212 °C
RTI Elec		UL 746	180 °C
RTI Imp		UL 746	170 °C
RTI Str		UL 746	180 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C	ASTM D570	0.90 %
Water absorption rate	Water absorption rate	24hr	ASTM D570	0.16 %
Shrinkage rate	MD：3.20mm	Internal Method	0.20-0.40 %
melt mass-flow rate	337°C/6.6kg	ASTM D1238	5.3 g/10min

Electrical performance	Test Condition	Test Method	Test Result
Hot wire ignition	HWI	UL 746	PLC 1
High voltage arc tracing rate	HVTR	UL 746	PLC 3
High arc combustion index	HAI	UL 746	PLC 4
Compared to the anti leakage trace index	CTI	UL 746	PLC 4
Arc resistance		ASTM D495	PLC6
Dissipation factor	2.45GHz	ASTM D150	5.3E-03
Dissipation factor	Dissipation factor	1kHz	ASTM D150	1.5E-03
Volume resistivity		ASTM D257	3E+16 ohms·cm
Dielectric strength	1.60mm,inAir	ASTM D149	25 KV/mm
Dielectric strength	Dielectric strength	1.60mm,in Oil	ASTM D149	30 KV/mm
Dielectric constant	1kHz	ASTM D150	3.70

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ASTM D785	114

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.