PA66 Leona™ 13G50 BK ASAHI JAPAN

361

Unit Price:US$ 4,190 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
75.5MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Fatigue resistance｜High rigidity｜Creep resistance｜high strength
Application Areas:Electrical applications｜Automotive Applications｜Gears
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch		ISO 179	无断裂
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Taber abraser	1000 Cycles	ASTM D1044	--	mg
bending strength	23°C	ISO 178	371	Mpa
bending strength	bending strength	--	ASTM D790	390	Mpa
Bending modulus	23°C	ISO 178	13600	Mpa
Bending modulus	Bending modulus	--	ASTM D790	14500	Mpa
elongation	Break, 23°C	ISO 527-2	2.0	%
elongation	elongation	Break	ASTM D638	2.5	%
tensile strength	--	ASTM D638	235	Mpa
tensile strength	tensile strength	Break, 23°C	ISO 527-2	237	Mpa
Tensile modulus	23°C	ISO 527-2	16900	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
thermal conductivity			0.40	W/m/K
Linear coefficient of thermal expansion	Flow	ASTM D696	2.0E-5	cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	255	°C
	Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	250	°C
	Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ASTM D648	260	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	--	%
Water absorption rate	Water absorption rate	Saturation, 23°C		--	%
Shrinkage rate	Flow	Internal Method	0.40	%
Shrinkage rate	Shrinkage rate	横向Flow	Internal Method	0.70	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257	1.0E+15	ohms
Volume resistivity	--	ASTM D257	1.0E+15	ohms·cm
Volume resistivity	Volume resistivity	23°C	IEC 60093	1.0E+15	ohms·cm
Dielectric strength		ASTM D149	21	KV/mm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R -Sale	ISO 2039-2	118
	Rockwell hardness	M -Sale	ISO 2039-2	95
		Rockwell hardness	R-Scale	ASTM D785	118
		Rockwell hardness	Rockwell hardness	M-Scale	ASTM D785	95

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.