optical performance	Test Condition	Test Method	Test Result	Test Unit
Transmittance rate	2.54 mm	ASTM D1003	88	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23℃	ASTM D256	801	J/m
Suspended wall beam without notch impact strength	/，23℃	ASTM D4812	3204	J/m
Instrumented dart impact energy 23 ℃ (73 ℉) total energy	/	ASTM D3763	63	J
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Type I, 5，Yield	ASTM D638	62	Mpa
tensile strength	tensile strength	Type I, 5，Break	ASTM D638	68	Mpa
elongation	Type I, 5，Yield	ASTM D638	7	%
Elongation at Break	Type I, 5	ASTM D638	130	%
bending strength	1.3 mm/min/，Yield	ASTM D790	96	Mpa
Bending modulus	1.3 mm/	ASTM D790	2340	Mpa
thermal properties	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	Rate B/50	ASTM D1525	154	°C
RTI Imp		UL 746B	130	°C
RTI Elec		UL 746B	130	°C
RTI Imp		UL 746B	130	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	/，300℃/1.2 kg	ASTM D1238	10.5	g/10min
Shrinkage rate	flow, 3.2	Internal	0.5-0.7
Water absorption rate	24 hours	ASTM D570	0.15
	Water absorption rate	equilibriu	ASTM D570	0.58
	Water absorption rate	Water absorption rate	equilibriu	ASTM D570	0.35
Bi Rong	/	ASTM D792	0.83
hardness	Test Condition	Test Method	Test Result	Test Unit
Hardness (Rockwell M)		ASTM D 785	70	M
Hardness (Rockwell R)		ASTM D 785	118	R

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.