PA46 Stanyl®  TE 200 S6 DSM JAPAN

248
  • Unit Price:US$ 6,450 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    42MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Glass fiber reinforcedThermal stability
  • Application Areas:Home appliance componentsElectronic and electrical components
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

mechanical propertiesTest ConditionTest MethodTest Result
Tensile strainBreak, 200°CISO 527-227 %
Tensile strainBreak, 180°CISO 527-228 %
Tensile strainBreak, 160°CISO 527-229 %
Tensile strainBreak, 120°CISO 527-230 %
Tensile strainBreakISO 527-24.5 %
tensile strengthBreak, 200°CISO 527-230.0 Mpa
tensile strengthBreak, 180°CISO 527-232.0 Mpa
tensile strengthBreak, 160°CISO 527-235.0 Mpa
tensile strengthBreak, 120°CISO 527-245.0 Mpa
tensile strengthBreakISO 527-290.0 Mpa
Tensile modulus200°CISO 527-2740 Mpa
Tensile modulus180°CISO 527-2800 Mpa
Tensile modulus160°CISO 527-2900 Mpa
Tensile modulus120°CISO 527-21000 Mpa
Tensile modulus--ISO 527-24700 Mpa
thermal performanceTest ConditionTest MethodTest Result
Melting temperatureISO 11357-3295 °C
Hot deformation temperature1.8 MPa, UnannealedISO 75-2/A235 °C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateEquilibrium, 23°C, 50% RHISO 622.6 %
Shrinkage rateFlowISO 294-41.3 %
Shrinkage rate横向FlowISO 294-41.7 %
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.