'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC LUX2114-WH5G007X SABIC INNOVATIVE NANSHA
241
- Unit Price:US$ 4,158 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D1822 | 546 | kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 65 | kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| 23°C | ASTM D256 | 600 | J/m | |
| -30°C | ISO 180/1A | 11 | kJ/m² | |
| 23°C | ISO 180/1A | 65 | kJ/m² | |
| ASTM D4812 | 3200 | J/m | ||
| -30°C | ISO 180/1U | 无断裂 | ||
| 23°C | ISO 180/1U | 无断裂 | ||
| Dart impact | 23°C | ASTM D3029 | 169 | J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 12 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.750165mm | UL 94 | V-2 | |
| Burning wire flammability index | 0.750mm | IEC 60695-2-12 | 750 | °C |
| 1.50mm | IEC 60695-2-12 | 850 | °C | |
| Hot filament ignition temperature | 0.750mm13 | IEC 60695-2-13 | 875 | °C |
| 1.50mm | IEC 60695-2-13 | 850 | °C | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| tensile strength | Yield | ASTM D638 | 62.1 | Mpa |
| Break | ASTM D638 | 65.5 | Mpa | |
| elongation | Yield | ASTM D638 | 7.0 | % |
| Break | ASTM D638 | 110 | % | |
| Bending modulus | 50.0mmSpan | ASTM D790 | 2340 | Mpa |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 93.1 | Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | ASTM D1044 | 10.0 | mg |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| RTI Imp | UL 746 | 80.0 | °C | |
| RTI Elec | UL 746 | 80.0 | °C | |
| thermal conductivity | ASTMC177 | 0.25 | W/m/K | |
| specific heat | ASTMC351 | 1260 | J/kg/°C | |
| Linear coefficient of thermal expansion | MD：-40to95°C | ASTME831 | 6.8E-05 | cm/cm/°C |
| Ball Pressure Test | 125°C | IEC 60695-10-2 | Pass | |
| Vicat softening temperature | ASTM D152512 | 154 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTM D648 | 132 | °C |
| 0.45MPa,Unannealed,6.40mm | ASTM D648 | 138 | °C | |
| RTI | UL 746 | 80.0 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | MD：3.20mm | Internal Method | 0.50-0.70 | % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 18 | g/10min |
| Specific volume | ASTM D792 | 0.830 | cm³/g | |
| Outdoor applicability | UL 746C | f2 | ||
| Water absorption rate | Equilibrium,100°C | ASTM D570 | 0.58 | % |
| Equilibrium,23°C | ASTM D570 | 0.35 | % | |
| 24hr | ASTM D570 | 0.15 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dissipation factor | 1MHz | ASTM D150 | 0.010 | |
| 60Hz | ASTM D150 | 9E-04 | ||
| 50Hz | ASTM D150 | 9E-04 | ||
| Dielectric constant | 1MHz | ASTM D150 | 2.96 | |
| 60Hz | ASTM D150 | 3.17 | ||
| 50Hz | ASTM D150 | 3.17 | ||
| Dielectric strength | 3.20mm,inAir | ASTM D149 | 15 | KV/mm |
| Volume resistivity | ASTM D257 | >1.0E+17 | ohms·cm | |
| Compared to the anti leakage trace index | CTI | UL 746 | PLC 3 | |
| Hot wire ignition | HWI | UL 746 | PLC 3 | |
| High arc combustion index | HAI | UL 746 | PLC 1 | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M-Scale | ASTM D785 | 70 | |
| R-Scale | ASTM D785 | 118 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.