PA66 Zytel® 80G25HS BK117 DUPONT USA

276

Unit Price:US$ 4,550 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
76MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Resistance to oxidation｜Glass fiber reinforced
Application Areas:Electronic and electrical accessories｜Automotive components
Color:--
Grade:Enhanced level

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			PA66.25％玻纤增强.增韧.热稳定.注塑树脂
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	83	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	89	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
FMVSS flammability		FMVSS302	B
Burning rate	1.00mm	ISO 3795	<100	mm/min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ASTM D790/ISO 178	6000	kg·cm/cm(J/M)ft·lb/in
tensile strength		ASTM D638/ISO 527	122	kg/cm²(MPa)[Lb/in²]
Tensile modulus		ASTM D638/ISO 527	6900	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	4	%
Impact strength of cantilever beam gap		ASTM D256/ISO 179	89	kg·cm/cm(J/M)ft·lb/in
	Impact strength of cantilever beam gap		ASTM D256/ISO 179	83	kg·cm/cm(J/M)ft·lb/in
		Impact strength of cantilever beam gap		ASTM D256/ISO 179	14	kg·cm/cm(J/M)ft·lb/in
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	22	kg·cm/cm(J/M)ft·lb/in
Bending modulus		ISO 178	6000	Mpa
Tensile strain	Break	ISO 527-2	4.0	%
tensile strength	Break	ISO 527-2	120	Mpa
Tensile modulus		ISO 527-2	7000	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	HDT	ASTM D648/ISO 75	240	℃（℉）
Melting temperature			262	℃（℉）
Hot deformation temperature	HDT	ASTM D648/ISO 75	258	℃（℉）
Melting temperature		ISO 11357-3	262	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	240	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	258	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.25
Shrinkage rate		ASTM D955	0.3	%
Top out temperature			210	°C
Shrinkage rate	MD	ISO 294-4	0.30	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	0.80	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.