EAA PRIMACOR™ 5980I DOW USA

696

Unit Price:US$ 9,334 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
35MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High gloss
Application Areas:Power tools
Color:--
Grade:Hot melt grade

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190℃/2.16kg	ASTM D-1238	300	g/10min
Monomer content		Internal Method	20.5	%
melt mass-flow rate	190℃/2.16kg	ISO 1133	300	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Elongation at Break	Compression Molded	ISO 527-2	390	%
Elongation at Break	Elongation at Break	Compression Molded	ASTM D-638	390	%
tensile strength	Compression Molded，Break	ISO 527-2	9.65	MPa
tensile strength	tensile strength	Compression Molded，Break	ASTM D-638	9.65	MPa
Tensile modulus	Compression Molded，2% Secant	ISO 527-2	33.1	MPa
Tensile modulus	Tensile modulus	Compression Molded，2% Secant	ASTM D-638	33.1	MPa
elongation	Break,Compression Molded	ASTMD638	390	%
tensile strength	Break,Compression Molded	ASTMD638	9.65	Mpa
Tensile modulus	Compression Molded，2%Secant	ASTMD638	33.1	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		Internal Method	77.2	℃
Vicat softening temperature		ISO 306	42.2	℃
Vicat softening temperature	Vicat softening temperature		ASTM D-1525	42.2	℃
Melting temperature		Internal Method	77.2	°C
Vicat softening temperature		ASTMD1525	42.2	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Content of comonomer		Internal Method	20.5	%
melt mass-flow rate	190°C/2.16kg3	ASTMD1238	300	g/10min
melt mass-flow rate	melt mass-flow rate	125°C/2.16kg2	ASTMD1238	14	g/10min
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	ShoreD	ASTMD2240	50

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.