'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC LEXAN™ HPS1-1125 SABIC INNOVATIVE US
271
- Unit Price:US$ 8,360 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :Guangzhou port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility
- Application Areas:medical care｜medicine
- Color:--
- Grade:Injection grade
Technical Data Sheet
| optical performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Refractive index | ASTM D542 | 1.586 | ||
| transmissivity | 2540μm | ASTM D1003 | 88.0 | % |
| turbidity | 2540μm | ASTM D1003 | 1.0 | % |
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 10 | kJ/m² |
| 23°C | ISO 179/1eA | 12 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 | kJ/m² |
| 23°C | ISO 180/1A | 12 | kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak | |
| 23°C | ISO 180/1U | NoBreak | ||
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 54.2 | J |
| 23°C | ASTM D3029 | 169 | J | |
| Impact strength of cantilever beam gap | ASTM D1822 | 378 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Extreme Oxygen Index | ISO 4589-2 | 25 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| elongation | Yield | ASTM D638 | 6.0 | % |
| Tensile strain | Yield | ISO 527-2/50 | 6.0 | % |
| elongation | Break | ASTM D638 | 120 | % |
| Tensile strain | Break | ISO 527-2/50 | 70 | % |
| Bending modulus | 50.0mmSpan | ASTM D790 | 2310 | Mpa |
| ISO 178 | 2300 | Mpa | ||
| bending strength | ISO 178 | 90.0 | Mpa | |
| Yield,50.0mmSpan | ASTM D790 | 93.1 | Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | ASTM D1044 | 10.0 | mg |
| Tensile modulus | ASTM D638 | 2380 | Mpa | |
| ISO 527-2/1 | 2350 | Mpa | ||
| tensile strength | Yield | ASTM D638 | 62.1 | Mpa |
| Yield | ISO 527-2/50 | 63.0 | Mpa | |
| Break | ASTM D638 | 65.5 | Mpa | |
| Break | ISO 527-2/50 | 50.0 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| thermal conductivity | ASTMC177 | 0.19 | W/m/K | |
| ISO 8302 | 0.20 | W/m/K | ||
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTM D648 | 138 | °C |
| 0.45MPa,Unannealed,100mmSpan | ISO 75-2/Be | 133 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTM D648 | 127 | °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO 75-2/Ae | 121 | °C | |
| Vicat softening temperature | -- | ISO 306/B50 | 139 | °C |
| -- | ISO 306/B120 | 140 | °C | |
| Ball Pressure Test | 125°C | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40to95°C | ASTME831 | 6.8E-05 | cm/cm/°C |
| MD：23to80°C | ISO 11359-2 | 7E-05 | cm/cm/°C | |
| specific heat | ASTMC351 | 1260 | J/kg/°C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | MD：3.20mm | Internal Method | 0.50-0.70 | % |
| Water absorption rate | 24hr | ASTM D570 | 0.15 | % |
| Equilibrium,23°C | ASTM D570 | 0.35 | % | |
| Equilibrium,100°C | ASTM D570 | 0.58 | % | |
| Specific volume | ASTM D792 | 0.835 | cm³/g | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 25 | g/10min |
| Melt Volume Flow Rate (MVR) | 300°C/1.2kg | ISO 1133 | 23.0 | cm3/10min |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | IEC 60093 | >1.0E+15 | ohms | |
| Volume resistivity | ASTM D257 | >1.0E+17 | ohms·cm | |
| IEC 60093 | >1.0E+15 | ohms·cm | ||
| Dielectric strength | 3.20mm,inAir | ASTM D149 | 15 | KV/mm |
| 3.20mm,in Oil | IEC 60243-1 | 17 | KV/mm | |
| Dielectric constant | 50Hz | ASTM D150 | 3.17 | |
| 60Hz | ASTM D150 | 3.17 | ||
| 1MHz | ASTM D150 | 2.96 | ||
| Relative permittivity | 50Hz | IEC 60250 | 2.70 | |
| 60Hz | IEC 60250 | 2.70 | ||
| 1MHz | IEC 60250 | 2.70 | ||
| Dissipation factor | 50Hz | ASTM D150 | 9E-04 | |
| 60Hz | ASTM D150 | 9E-04 | ||
| 1MHz | ASTM D150 | 0.010 | ||
| 50Hz | IEC 60250 | 1E-03 | ||
| 60Hz | IEC 60250 | 1E-03 | ||
| 1MHz | IEC 60250 | 0.010 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M-Sale | ASTM D785 | 70 | |
| R-Sale | ASTM D785 | 118 | ||
| Ball Pressure Test | H358/30 | ISO 2039-1 | 95.0 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.