LCP VECTRA®  V143XL CELANESE USA

182
  • Unit Price:US$ 6,251 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    50MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Glass fiber reinforcedenhance
  • Application Areas:Automotive ApplicationsElectrical applications
  • Color:--
  • Grade:Enhanced level

Technical Data Sheet Compare

thermal performanceTest ConditionTest MethodTest Result
Heat Deflection Temperature1.8 MPa, 未退火ISO 75-2/A260 °C
melting temperatureISO 11357-3335 °C
Linear coefficient of thermal expansion流动ISO 11359-28.0E-6 cm/cm/°C
Linear coefficient of thermal expansion横向ISO 11359-23.1E-5 cm/cm/°C
Impact resistanceTest ConditionTest MethodTest Result
Impact strength of cantilever beam gap23°CISO 180/1A9.0 kJ/m²
Physical propertiesTest ConditionTest MethodTest Result
densityISO 11831.67 g/cm³
shrinkage rate横向流量ISO 294-40.60 %
shrinkage rate流量ISO 294-40.30 %
Water absorption rate饱和, 23°CISO 620.044 %
Water absorption rate平衡, 23°C, 50% RHISO 620.015 %
Electrical performanceTest ConditionTest MethodTest Result
Surface ResistivityIEC 600931.0E+17 ohms
volume resistivityIEC 600931.0E+16 ohms·cm
dielectric strengthIEC 60243-133 KV/mm
relative permittivity1 MHzIEC 602503.50
Dissipation Factor1 MHzIEC 602500.016
injectionTest ConditionTest MethodTest Result
drying temperature150 °C
drying time4.0 to 24 hr
Suggested maximum moisture content0.010 %
Hopper temperature20 to 30 °C
Temperature at the rear of the barrel315 to 325 °C
Temperature in the middle of the barrel320 to 330 °C
Temperature at the front of the material cylinder325 to 335 °C
Spray nozzle temperature335 to 345 °C
Processing (melt) temperature335 to 345 °C
mold temperature80 to 120 °C
injection speed快速
Back pressure< 3.00 Mpa
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusISO 527-2/1A16000 Mpa
tensile strength断裂ISO 527-2/1A/5150 Mpa
Tensile strain断裂ISO 527-2/1A/51.3 %
flexural modulus23°CISO 17815700 Mpa
bending strength23°CISO 178225 Mpa
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.