HIPS HIPS-514 SECCO SHANGHAI
269
- Unit Price:US$ 1,157 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:58.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:heat-resisting｜High impact resistance
- Application Areas:Toy｜Electronic field｜Electrical field
- Color:--
- Grade:Impact resistant grade
Material Certification
Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | HDT | ASTM D648/ISO 75 | 74 ℃（℉） |
| Vicat softening temperature | ASTM D1525/ISO R306 | 85 ℃（℉） | |
| Hot deformation temperature | 1.82MPa | ISO 75-2/1993 | 74 °C |
| Vicat softening temperature | B50/oil | ISO 306/1994 | 85 °C |
| Basic Performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 200℃/5Kg | ISO 1133/1997 | 10 g/10min |
| density | ISO 1183/1987 | 1030 kg/m |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.03 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 10 g/10min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 100 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 750 kg·cm/cm(J/M)ft·lb/in | ||
| Elongation at Break | ASTM D638/ISO 527 | 50 % | |
| tensile strength | ASTM D638/ISO 527 | 23 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | 2mm/min | ISO 178/1993 | 2000 Mpa |
| elongation | 50mm/min | ISO 527-2/1993 | 50 % |
| Impact strength of cantilever beam gap | ISO 180/1993 | 100 J/m | |
| tensile strength | Yield | ISO 527-2/1993 | 23 Mpa |
| Impact strength of cantilever beam gap | ISO 180/1993 | 750 J/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.