PC LNP™ STAT-KON™ DS00361C BK1B511BZDD SABIC INNOVATIVE US

215

Unit Price:US$ 8,531 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
15MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Non chloro non bromine flame retardant｜electromagnetic shielding ｜RF shielding
Application Areas:Medical and nursing supplies｜Electronic and Electrical Applications｜Aerospace Applications｜Plastic bag
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ASTM D4812	1800 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C2	ISO 180/1U	85 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	2.1 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	2800 Mpa
tensile strength	Yield	ISO 527-2	57.0 Mpa
tensile strength	tensile strength	Break	ISO 527-2	55.0 Mpa
Tensile strain	Yield	ISO 527-2	3.8 %
Tensile strain	Tensile strain	Break	ISO 527-2	4.0 to 8.0 %
Bending modulus		ISO 178	2600 Mpa
bending strength		ISO 178	80.0 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			120 °C
drying time			4.0 hr
Suggested maximum moisture content			0.020 %
Temperature at the rear of the barrel			295 to 305 °C
Temperature in the middle of the barrel			310 to 320 °C
Temperature at the front of the material cylinder			320 to 330 °C
Processing (melt) temperature			305 to 325 °C
Mold temperature			95 to 120 °C
Back pressure			0.200 to 0.300 Mpa
Screw speed			30 to 60 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span	ISO 75-2/Bf	136 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span	ISO 75-2/Af	125 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ISO 11359-2	6.7E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	5.6E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	横向Flow : 24hr	ISO 294-4	0.50 %
Shrinkage rate	Shrinkage rate	Flow : 24hr	ISO 294-4	0.40 - 0.70 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257	1.0E+2 - 1.0E+3 ohms
Volume resistivity		ASTM D257	1.0E+4 ohms·cm
Electromagnetic shielding effectiveness (EMI)	3.00 mm	Internal Method	40 to 55 dB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LNP™ STAT-KON™ DS00361C BK1B511BZDD SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet