PP-R TOPILENE® R200P HYOSUNG KOREA
370
- Unit Price:US$ 1,411 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:24MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High temperature resistance｜High voltage resistance｜Chemical stability performance｜Heat resistance｜high strength
- Application Areas:Building water supply system｜Floor heating system｜Radiator heating｜Chemical tubing｜Agricultural pipe｜Pipe fittings
- Color:--
- Grade:Pipe grade
Technical Data Sheet
Compare
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 0.91 g/cm³ | |
| melt mass-flow rate | ASTM D-1238 | 0.2 g/10min | |
| ASTM D-1238 | 0.4 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D-638 | 230 kg/cm2 | |
| Impact strength of cantilever beam gap | ASTM D-256 | No break kg·cm/cm | |
| Flexural modulus | ASTM D-790 | 8.500 kg/cm2 | |
| Impact strength of cantilever beam gap | ASTM D-256 | 3 kg·cm/cm | |
| elongation | ASTM D-638 | ＞400 % | |
| tensile strength | ASTM D-638 | 270 kg/cm2 | |
| Volume resistivity | HS Method | ＞1013 Ω | |
| Impact strength of cantilever beam gap | ASTM D-256 | 8 kg·cm/cm | |
| tensile strength | ASTM D638/ISO 527 | 270 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 75 | |
| Flexural modulus | ASTM D790/ISO 178 | 9000 % | |
| elongation at break | ASTM D638/ISO 527 | ＞400 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 0.91 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 0.25 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | Dilatometer | 1.5×10-4 | |
| vicat | ASTM D-1525 | 130 °C | |
| melting temperature | HS Method | 141 °C | |
| 141 ℃（℉） | |||
| vicat | ASTM D1525/ISO R306 | 130 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.