PC Makrolon® ET3113 COVESTRO GERMANY
185
- Unit Price:US$ 2,154 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:50MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Weather resistance｜Hydrolysis resistance
- Application Areas:Electrical field｜Electronic field｜Automotive sector｜Other sheets｜PC board
- Color:--
- Grade:--
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.20 g/cm³ | |
| Apparent density | ISO 60 | 0.66 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 6.5 g/10 min | |
| Melt volume flow rate | ISO 1133 | 6.00 cm3/10min | |
| Shrinkage rate | ISO 2577 | 0.60 - 0.80 % | |
| ISO 2577 | 0.60 - 0.80 % | ||
| ISO 294-4 | 0.75 % | ||
| ISO 294-4 | 0.70 % | ||
| Water absorption rate | ISO 62 | 0.30 % | |
| ISO 62 | 0.12 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 2039-1 | 113 Mpa |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ISO 489 | 1.587 | |
| transmissivity | ISO 13468-2 | 89.0 % | |
| ISO 13468-2 | 89.0 % | ||
| ISO 13468-2 | 88.0 % | ||
| ISO 13468-2 | 87.0 % | ||
| Haze ratio | ISO 14782 | < 0.80 % | |
| electrolytic corrosion | IEC 60426 | A1 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| UL 94 | V-2 | ||
| Burning wire flammability index | IEC 60695-2-12 | 875 °C | |
| IEC 60695-2-12 | 875 °C | ||
| IEC 60695-2-12 | 960 °C | ||
| Hot filament ignition temperature | IEC 60695-2-13 | 875 °C | |
| IEC 60695-2-13 | 875 °C | ||
| IEC 60695-2-13 | 900 °C | ||
| Limiting Oxygen Index | ISO 4589-2 | 28 % | |
| Application of Flame from Small Burner | DIN 53438-1 | K1. F1 | |
| flash temperature | ASTM D1929 | 480 °C | |
| UL flame retardant rating | IEC 60695-11-5 | 1.0 min | |
| IEC 60695-11-5 | 2.0 min | ||
| IEC 60695-11-5 | 0.1 min | ||
| IEC 60695-11-5 | 2.0 min | ||
| IEC 60695-11-5 | 0.2 min | ||
| auto-ignition temperature | ASTM D1929 | 550 °C | |
| burning rate | ISO 3795 | passed |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2350 Mpa | |
| tensile strength | ISO 527-2/50 | 65.0 Mpa | |
| ISO 527-2/50 | 70.0 Mpa | ||
| Tensile strain | ISO 527-2/50 | 6.3 % | |
| ISO 527-2/50 | 130 % | ||
| Nominal tensile fracture strain | ISO 527-2/50 | > 50 % | |
| Tensile creep modulus | ISO 899-1 | 2200 Mpa | |
| ISO 899-1 | 1900 Mpa | ||
| Flexural modulus | ISO 178 | 2350 Mpa | |
| bending strength | ISO 178 | 96.0 Mpa | |
| ISO 178 | 72.0 Mpa | ||
| ISO 178 | 7.2 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 18 kJ/m² | |
| ISO 179/1eA | 80 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
| ISO 179/1eU | 无断裂 | ||
| ISO 179/1eU | 无断裂 | ||
| Impact strength of cantilever beam gap | ISO 180/A | 20 kJ/m² | |
| ISO 180/A | 70 kJ/m² | ||
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 70.0 J | |
| ISO 6603-2 | 60.0 J | ||
| Multi axis Instrumented Peak Impact Force | ISO 6603-2 | 6500 N | |
| ISO 6603-2 | 5600 N |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water vapor permeability | ISO 15106-1 | 15 g/m²/24 hr | |
| Carbon dioxide transmittance | ISO 2556 | 16900 cm³/m²/bar/24 hr | |
| gas transmission rate | ISO 2556 | 3800 cm³/m²/bar/24 hr | |
| ISO 2556 | 510 cm³/m²/bar/24 hr | ||
| ISO 2556 | 120 cm³/m²/bar/24 hr | ||
| ISO 2556 | 2760 cm³/m²/bar/24 hr | ||
| ISO 2556 | 650 cm³/m²/bar/24 hr |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1.0E+16 ohms | |
| Volume resistivity | IEC 60093 | 1.0E+16 ohms·cm | |
| dielectric strength | IEC 60243-1 | 34 KV/mm | |
| IEC 60250 | 3.10 | ||
| IEC 60250 | 3.00 | ||
| Dissipation Factor | IEC 60250 | 8.0E-4 | |
| IEC 60250 | 0.010 | ||
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| IEC 60112 | PLC 4 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ISO 75-2/B | 141 °C | |
| ISO 75-2/A | 128 °C | ||
| Glass Transition Temperature | ISO 11357-2 | 148 °C | |
| vicat | ISO 306/B50 | 148 °C | |
| ISO 306/B120 | 149 °C | ||
| Ball Pressure Test | IEC 60695-10-2 | 通过 | |
| ISO 11359-2 | 6.5E-5 cm/cm/°C | ||
| ISO 11359-2 | 6.5E-5 cm/cm/°C | ||
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| RTI Elec | UL 746 | 125 °C | |
| RTI Imp | UL 746 | 115 °C | |
| RTI | UL 746 | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.