LCP VECTRA® A115 CELANESE USA

266

Unit Price:US$ 9,960 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
50.5MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Halogen-free｜Flame retardant
Application Areas:Fitness equipment｜Home appliance components｜Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	61	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	48	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Compressive stress	1% Strain	ISO 604	85.0	Mpa
Compressive modulus		ISO 604	10000	Mpa
bending strength	23°C	ISO 178	250	Mpa
Bending modulus	23°C	ISO 178	12400	Mpa
Tensile strain	Break	ISO 527-2/1A/5	3.1	%
tensile strength	Break	ISO 527-2/1A/5	200	Mpa
Tensile modulus		ISO 527-2/1A	12000	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			150	°C
drying time			4.0 to 6.0	hr
Suggested maximum moisture content			0.010	%
Hopper temperature			20 to 30	°C
Temperature at the rear of the barrel			270 to 280	°C
Temperature in the middle of the barrel			275 to 285	°C
Temperature at the front of the material cylinder			280 to 290	°C
Spray nozzle temperature			290 to 300	°C
Processing (melt) temperature			285 to 295	°C
Mold temperature			80 to 120	°C
Injection speed			快速
Back pressure			< 3.00	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.8E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.0E-5	cm/cm/°C
Melting temperature		ISO 11357-3	280	°C
Vicat softening temperature		ISO 306/B50	162	°C
Hot deformation temperature	8.0 MPa, Unannealed	ISO 75-2/C	157	°C
	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	230	°C
	Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	250	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	3.0E-3	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	6.0E-3	%
Shrinkage rate	Flow	ISO 294-4	0.10	%
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	0.40	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Relative permittivity	100 Hz	IEC 60250	3.50
Relative permittivity	Relative permittivity	1 MHz	IEC 60250	3.00
Dissipation factor	100 Hz	IEC 60250	0.020
Dielectric strength		IEC 60243-1	34	KV/mm
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Dissipation factor	1 MHz	IEC 60250	0.018
Arc resistance		Internal Method	135	sec
Compared to the anti leakage trace index		IEC 60112	PLC 3
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M -Sale	ISO 2039-2	80

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top