PA6 Durethan® BKV35H2.0 ENVALIOR WUXI
255
- Unit Price:US$ 3,045 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:88.1MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:35% glass fiber reinforced｜Easy to flow｜Thermal stability rating
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 1.80MPa | ISO 75-1 | 210 °C |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 260℃；2.16kg | ISO 1133 | 43 cm3/10min |
| Fiberglass content | ISO 3451-1 | 35 % | |
| density | ISO 1183 | 1.396 g/cm³ |
| machinability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Injection speed | ISO 294 | 200 mm/s | |
| Mold temperature | ISO 294 | 80 °C | |
| Melt Temperature | ISO 294 | 260 °C |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Bending modulus | 2mm/min | ISO 178 | 9500(5900) Mpa |
| Elongation at Break | 5mm/min | ISO 527-1 | 3.0 % |
| Tensile stress | 2mm/min，0.035 | ISO 178 | 270(150) Mpa |
| Tensile modulus | 1mm/min | ISO 527-1 | 10500(6700) Mpa |
| bending strength | 2mm/min | ISO 178 | 4.0(6.0) % |
| 2mm/min | ISO 178 | 280(180) Mpa | |
| tensile strength | 5mm/min | ISO 527-1 | 190(115) Mpa |
| Impact strength of cantilever beam gap | 23℃ | ISO 180-1U | 75 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.