Material Properties:wear resistant｜High mobility｜transparent｜High temperature resistance｜Forming method: extrusion｜Excellent wear resistance
Application Areas:Electronic field｜Electrical field
Color:--
Grade:Heat resistant grade

Material Certification

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ASTM D-1238	3.5	g/10min
Water absorption rate	浸水24hrs后增重	ASTM D-570	0.3	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	Izod 研磨Notched	ASTM D256	1.2(12.3)	kgf-cm/cm(J/m)
bending strength	横跨比=16	ASTM D-790	1050(103)	Kgf/cm
Bending modulus		ASTM D-790	32000	Kgf/cm
Impact strength of cantilever beam gap	落锤(15.2×15.2×0.3cm重1.4kg半径0.64cm)	ASTM D256	14(1.4)	kg-cm(J)
tensile strength	初级Strain速度0.1cm/cm/min	ASTM D-638	720(70)	Kgf/cm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Temperature range for use	与残余应力大小有关		85-102	°C
Hot deformation temperature	2℃/min,18.6kgf/cm，Annealed	ASTM D-648	102	°C
Glass transition temperature	Tg		108	°C
Vicat softening temperature	50℃/hr,1kg	ASTM D-1525，未退火	111	°C
Vicat softening temperature	Vicat softening temperature	50℃/hr,5kg	ASTM D-1525，未退火	104	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ASTM D-758(M级)	97
Transmittance rate		ASTM D-1003	92	%
density		ASTM D-792	1.19
Refractive index		ASTM D-542	1.49
Shrinkage rate	(冷模/冷件),48hrs	ASTM D-935	0.2-0.6	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.