PC LEXAN™ EXL1414 WH7E246 SABIC INNOVATIVE NANSHA
152
- Unit Price:US$ 3,421 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:38MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Processability｜Moderate liquidity｜Ductility｜copolymer｜Good demolding performance
- Application Areas:Bottle cap｜Home appliance components｜Electrical applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 121 | |
| ASTM D785 | 89 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI Str | UL 746 | 125 °C | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 120 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 7.2E-05 cm/cm/°C | |
| ISO 11359-2 | 7.2E-05 cm/cm/°C | ||
| ASTME831 | 7.5E-05 cm/cm/°C | ||
| ASTME831 | 7E-05 cm/cm/°C | ||
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| vicat | ISO 306/B120 | 146 °C | |
| ISO 306/B50 | 145 °C | ||
| ASTM D152510 | 145 °C | ||
| Heat Deflection Temperature | ASTM D648 | 124 °C | |
| ISO 75-2/Ae | 128 °C | ||
| ASTM D648 | 139 °C | ||
| ISO 75-2/Be | 140 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| IEC 60695-2-12 | 850 °C | ||
| UL flame retardant rating | UL 94 | HB | |
| Hot filament ignition temperature | IEC 60695-2-13 | 875 °C | |
| IEC 60695-2-13 | 875 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | ASTM D256 | 770 J/m | |
| ASTM D256 | 870 J/m | ||
| ISO 180/1A | 60 kJ/m² | ||
| ISO 180/1A | 70 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak | |
| Charpy Notched Impact Strength | ISO 179/1eA | 65 kJ/m² | |
| ISO 179/1eA | 70 kJ/m² | ||
| Dart impact | ASTM D3763 | 70.0 J | |
| Suspended wall beam without notch impact strength | ISO 180/1U | NoBreak | |
| ISO 180/1U | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | ASTM D150 | 2.68 | |
| ASTM D150 | 2.64 | ||
| Dissipation Factor | ASTM D150 | 1.2E-03 | |
| ASTM D150 | 9.3E-03 | ||
| volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 16 KV/mm | |
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | ISO 1133 | 9.00 cm3/10min | |
| shrinkage rate | 内部方法 | 0.40-0.80 % | |
| 内部方法 | 0.40-0.80 % | ||
| Water absorption rate | ISO 62 | 0.35 % | |
| ISO 62 | 0.15 % | ||
| melt mass-flow rate | ASTM D1238 | 10 g/10min | |
| density | ASTM D792 | 1.18 g/cm³ | |
| ISO 1183 | 1.19 g/cm³ |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| flexural modulus | ASTM D790 | 2230 Mpa | |
| ISO 178 | 2250 Mpa | ||
| Tensile strain | ISO 527-2/50 | 120 % | |
| elongation | ASTM D638 | 6.0 % | |
| Tensile strain | ISO 527-2/50 | 6.0 % | |
| elongation | ASTM D638 | 98 % | |
| tensile strength | ISO 527-2/50 | 60.0 Mpa | |
| Tensile modulus | ASTM D638 | 2020 Mpa | |
| ISO 527-2/1 | 2150 Mpa | ||
| tensile strength | ASTM D638 | 55.5 Mpa | |
| ISO 527-2/50 | 57.0 Mpa | ||
| ASTM D638 | 50.3 Mpa | ||
| bending strength | ISO 178 | 85.0 Mpa | |
| ASTM D790 | 92.4 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.