PC CALIBRE™ MEGARAD™ 2081-15 STYRON US
302
- Unit Price:US$ 9,882 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Medical grade
- Application Areas:Medical supplies｜Nursing supplies
- Color:--
- Grade:Medical grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 118 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,退火 | ASTM D648 | 139 °C |
| 0.45MPa | ISO 75-24 | 137 °C | |
| 1.8MPa,未退火 | ASTM D648 | 122 °C | |
| 1.8MPa,未退火 | ISO 75-2/A | 120 °C | |
| 1.8MPa,退火 | ASTM D648 | 136 °C | |
| 1.8MPa | ISO 75-24 | 123 °C | |
| vicat | -- | ASTM D152510 | 148 °C |
| -- | ISO 306/B50 | 143 °C | |
| 50°C/h,B(50N) | ISO 3064 | 143 °C | |
| Linear coefficient of thermal expansion | MD：-40到82°C | ASTM D696 | 6.8E-05 cm/cm/°C |
| MD：-- | ISO 178/1993 | 7E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Normal combustion performance with a thickness of 1.6mm | 1.60mm,UL | ISO 12104 | HB |
| UL flame retardant rating | 3.20mm | ISO 12104 | HB |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ASTMD542 | 1.586 | |
| transmissivity | ASTM D1003 | 89.0 % | |
| haze | ASTM D1003 | 1.0 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO 11334 | 12.0 cm3/10min |
| shrinkage rate | MD | ASTM D955 | 0.50-0.70 % |
| MD | ISO 294-4 | 0.50-0.70 % | |
| water absorption rate | 23°C,24hr | ASTMD570 | 0.15 % |
| 平衡,23°C,50%RH | ASTMD570 | 0.32 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 15 g/10min |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | -- | ASTM D257 | 2E+17 ohms·cm |
| -- | IEC 600934 | >1.0E+13 ohms·m | |
| dielectric strength | ASTMD1494 | 17 KV/mm | |
| dielectric constant | 60Hz | ASTM D150 | 3.00 |
| 1MHz | ASTMD150 | 3.00 | |
| 100Hz | IEC 602504 | 3.00 | |
| Dissipation Factor | 50Hz | ASTM D150 | 1E-03 |
| 1MHz | ASTMD150 | 2E-03 | |
| 100Hz | IEC 602504 | 1E-03 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 断裂5 | ASTM D638 | 68.3 Mpa |
| 断裂 | ISO 527-2/50 | 68.0 Mpa | |
| elongation | 屈服5 | ASTM D638 | 6.0 % |
| 屈服 | ISO 527-2/50 | 6.0 % | |
| 断裂5 | ASTM D638 | 150 % | |
| 断裂 | ISO 527-2/50 | 150 % | |
| 断裂 | ISO 527-24 | >50 % | |
| flexural modulus | --6 | ASTM D790 | 2410 Mpa |
| --7,8 | ISO 178 | 2400 Mpa | |
| bending strength | --6 | ASTM D790 | 96.5 Mpa |
| tensile modulus | --5 | ASTM D638 | 2210 Mpa |
| -- | ISO 527-2/50 | 2300 Mpa | |
| tensile strength | 屈服5 | ASTM D638 | 62.1 Mpa |
| 屈服 | ISO 527-2/50 | 62.0 Mpa | |
| bending strength | --7,8 | ISO 178 | 98.0 Mpa |
| Abrasion | ASTM D1044 | 45 % |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C,总能量 | ASTM D3763 | 81.3 J |
| Impact strength of cantilever beam gap | ASTM D1822 | 378 kJ/m² | |
| Charpy Notched Impact Strength | -30°C | SK | 无断裂 |
| 23°C | SK | 无断裂 | |
| Suspended wall beam without notch impact strength | 23°C | ASTMD256 | 无断裂 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.