PC INFINO® NH-1015V K24774 LOTTE KOREA

205

Unit Price:US$ 2,695 /MT
Packaging Specification:
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:enhance｜transparent
Application Areas:Home appliance applications｜Laptop
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	17 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	14 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	2.0mm	UL 94	5VB

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ASTM D638	64.0 Mpa
	tensile strength	Yield	ISO 527-2/50	61.0 Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	48.0 Mpa
Tensile strain	Break	ISO 527-2/50	45 %
Bending modulus		ASTM D790	2400 Mpa
Bending modulus	Bending modulus		ISO 178	2550 Mpa
bending strength		ASTM D790	87.0 Mpa
bending strength	bending strength		ISO 178	89.0 Mpa
Tensile modulus		ISO 527-2/50	2500 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	94.0 °C
	Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	102 °C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	86.0 °C
			Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	82.0 °C
			Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	97.0 °C
Vicat softening temperature	--	ISO 306/B50	100 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	103 °C
RTI Elec	1.5mm	UL 746	90.0 °C
RTI Imp	1.5mm	UL 746	85.0 °C
RTI Str	1.5mm	UL 746	90.0 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	220°C/10.0kg	ASTM D1238	30 g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ISO 1133	30 g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.50-0.70 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	118
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC INFINO® NH-1015V K24774 LOTTE KOREA

Material Description

Technical Data Sheet Compare

Technical Data Sheet