flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	V-0
Bar Flow Length	320°C, 500.0 μm		7.10	CM
Elongation at Break		ASTM D638	0.30	%
Weld Strength		ASTM D638	35.0	Mpa
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ASTM D638	165	Mpa
elongation	Break	ASTM D638	3.5	%
Bending modulus		ASTM D790	15000	Mpa
bending strength		ASTM D790	225	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	285	°C
Glass transition temperature			125	°C
Melting temperature			306	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	320°C/2.16 kg	ASTM D1238	84	g/10 min
Shrinkage rate	Flow : 1.00 mm		0.030	%
Shrinkage rate	Shrinkage rate	Across FlowFlow : 1.00 mm		0.40	%
Water absorption rate	Equilibrium, 40°C, 95%RH		0.80	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257	1.0E+16	ohms·cm
Dielectric strength		ASTM D149	30	KV/mm
Dielectric constant	10.0 GHz	ASTM D150	3.80
Dissipation factor	10.0 GHz	ASTM D150	0.010
Compared to the anti leakage trace index		UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.