PA66

PA66 Zytel® 70G30HSL BK039 DUPONT KOREA

268

Unit Price:US$ 3,214 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
52.2MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Hydrolysis resistance
Application Areas:Electrical appliances
Color:--
Grade:--

Technical Data Sheet

Filling analysis	Test Method	Test Result
Melt density		1.21 g/cm³
Specific Heat Capacity of Melt		2290 J/kg/°C
Thermal Conductivity of Melt		0.21 W/m/K
Emission of Organic Compounds	VDA 277	6.00 µgC/g
Odor	VDA 270	4.50

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB
Burning rate	1.00 mm	ISO 3795	24 mm/min
Extreme Oxygen Index		ISO 4589-2	24 %
FMVSS combustion rate		FMVSS 302	SE/B
Atomization	F-value (refraction)	ISO 6452	95 %
Atomization	Atomization	G-value (condensate)	ISO 6452	3.0E-4 g

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Break	ISO 527-2	3.5 %
tensile strength	Break	ISO 527-2	195 Mpa
Tensile modulus		ISO 527-2	9800 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
Drying time - hot air dryer			2.0 to 4.0 hr
Suggested maximum moisture content			0.20 %
Processing (melt) temperature			285 to 305 °C
Melt Temperature, Optimum			295 °C
Mold temperature			70 to 120 °C
Mold Temperature, Optimum			100 °C
Maintain pressure			50.0 to 100 Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00 s/mm
Maximum Screw Tangential Speed			12 m/min

thermal performance	Test Condition	Test Method	Test Result
Effective thermal diffusivity coefficient			6.85E-8 m²/s
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	9.5E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.8E-5 cm/cm/°C
Melting temperature		ISO 11357-3	262 °C
Glass transition temperature		ISO 11357-2	80.0 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	253 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	260 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	2.0 %
Water absorption rate	Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	6.9 %
Shrinkage rate	Flow	ISO 294-4	0.30 %
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	1.1 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index		IEC 60112	PLC 0
Compared to the anti leakage trace index	Compared to the anti leakage trace index	3.00 mm	UL 746	PLC 0
Dissipation factor	1 MHz	IEC 62631-2-1	0.016
Dissipation factor	Dissipation factor	100 Hz	IEC 62631-2-1	0.016
Volume resistivity		IEC 62631-3-1	1.0E+11 ohms·m
Surface resistivity		IEC 62631-3-2	-- ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Zytel® 70G30HSL BK039 DUPONT KOREA

Material Description

Technical Data Sheet Compare

Technical Data Sheet