PA66 Zytel® 70G50HSLA BK039B DUPONT USA
196
- Unit Price:US$ 3,648 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:101.6MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal stability｜Dimensional stability
- Application Areas:Electrical applications｜Fitness equipment
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | PA66.50％玻纤增强.热稳定.流动性.注射成型 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 253 ℃（℉） |
| melting temperature | 262 ℃（℉） | ||
| Glass Transition Temperature | ISO 11357-2 | 80.0 °C | |
| vicat | ISO 306/B50 | 255 °C | |
| melting temperature | ISO 11357-3 | 262 °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 9E-06 cm/cm/°C |
| MD：-40to23°C | ISO 11359-2 | 1.9E-05 cm/cm/°C | |
| MD：55to160°C | ISO 11359-2 | 8E-06 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 7.2E-05 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 5.8E-05 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 1E-04 cm/cm/°C | |
| TD：导热系数 | ISO 11359-2 | 0.46 W/m/K | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 261 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 255 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| 0.8mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 24 % | |
| FMVSS flammability | FMVSS302 | SE | |
| Fogging-G-value | condensate | ISO 6452 | 4E-04 g |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 6.50 µgC/g | |
| Odor | VDA270 | 3.00 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 90 kJ/m² |
| 23°C | ISO 179/1eU | 100 kJ/m² | |
| Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 10.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.57 | |
| MediumDensity | 1.40 g/cm³ | ||
| Ejection Temperature | 210 °C | ||
| SpecificHeatCapacity of Melt | 1870 J/kg/°C | ||
| ThermalConductivityofMelt | 0.31 W/m/K | ||
| shrinkage rate | TD | ISO 294-4 | 0.80 % |
| MD | ISO 294-4 | 0.30 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 4.2 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.2 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | -- ohms | |
| volume resistivity | IEC 60093 | 1E+15 ohms·cm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 16 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 95 kg·cm/cm(J/M)ft·lb/in | ||
| Elongation at break | ASTM D638/ISO 527 | 2.2 % | |
| Tensile modulus | ASTM D638/ISO 527 | 16800 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 245 kg/cm²(MPa)[Lb/in²] | |
| Tensile creep modulus | 1000hr | ISO 899-1 | -- Mpa |
| flexural modulus | ISO 178 | 16000 Mpa | |
| bending strength | ISO 178 | 400 Mpa | |
| Tensile modulus | ISO 527-2 | 17000 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 250 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.4 % |
| Tensile creep modulus | 1hr | ISO 899-1 | -- Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.