PEI ULTEM™ ATX200-51027 SABIC INNOVATIVE US

220

Unit Price:US$ 16,682 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Hydrolysis resistance｜Aging resistance
Application Areas:Bottle cap｜Automotive Applications｜Electrical applications
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Reverse notch impact	3.20 mm	ASTM D256	2100 J/m
Suspended wall beam without notch impact strength	23°C	ASTM D4812	2100 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	0.75 mm	UL 94	V-2

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield, 100 mm Span	ASTM D790	144 Mpa
Bending modulus	100 mm Span	ASTM D790	3170 Mpa
elongation	Break	ASTM D638	70 %
tensile strength	Yield	ASTM D638	96.0 Mpa

injection	Test Condition	Test Method	Test Result
Spray nozzle temperature			350 to 370 °C
Processing (melt) temperature			350 to 370 °C
Mold temperature			135 to 165 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm
Temperature at the front of the material cylinder			350 to 370 °C
Temperature in the middle of the barrel			345 to 365 °C
Temperature at the rear of the barrel			340 to 360 °C
Suggested injection volume			40 to 60 %
Suggested maximum moisture content			0.020 %
drying time			4.0 to 6.0 hr
drying temperature			135 °C

thermal performance	Test Condition	Test Method	Test Result
RTI		UL 746	115 °C
RTI Imp		UL 746	115 °C
RTI Elec		UL 746	115 °C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	190 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %
melt mass-flow rate	337°C/6.6 kg	ASTM D1238	24 g/10 min

Electrical performance	Test Method	Test Result
Hot wire ignition	UL 746	PLC 0
High arc combustion index	UL 746	PLC 4
Compared to the anti leakage trace index	UL 746	PLC 4

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.