PA6

PA6 Durethan® BKV50H3.0 000000 LANXESS GERMANY

324

Unit Price:US$ 2,940 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
67MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	95 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	95 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	90 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	HB
Burning wire flammability index	2.0mm	IEC 60695-2-12	650 °C
BurningBehavior	>1.00mm	ISO 3795	passed

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2/1	16800 Mpa
Bending strain	23°C		3.0 %
bending strength	23°C	ISO 178	360 Mpa
Bending modulus	23°C	ISO 178/A	15500 Mpa
Tensile strain	Break,23°C	ISO 527-2/5	3.0 %
tensile strength	Break,23°C	ISO 527-2/5	225 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	2E-05 cm/cm/°C
Melting temperature		ISO 11357-3	222 °C
Vicat softening temperature	--	ISO 306/B120	>200 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	>200 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	205 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	215 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.5 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	5.0 %
Shrinkage rate	MD:120°C,2hr,3.00mm3	ISO 2577	0.020 %
	Shrinkage rate	MD:280°C,3.00mm2	ISO 2577	0.16 %
		Shrinkage rate	TD:120°C,2hr,3.00mm3	ISO 294-4	0.050 %
		Shrinkage rate	Shrinkage rate	TD:280°C,3.00mm2	ISO 2577	0.85 %
Apparent density		ISO 60	0.70 g/cm³

Supplementary Information	Test Condition	Test Method	Test Result
ISO Shortcut		ISO 1874	PA6.GHR.14-160.GF50

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Durethan® BKV50H3.0 000000 LANXESS GERMANY

Material Description

Technical Data Sheet Compare

Technical Data Sheet