ABS Toyolac® 900-352A TORAY MALAYSIA
300
- Unit Price:US$ 2,576 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:18MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜High impact resistance
- Application Areas:household electrical appliances｜Electronic and electrical components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ASTM D785 | 108 |
| R计秤,23°C | ISO 2039-2 | 108 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTM D648 | 81.0 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 76.0 °C | |
| vicat | 90.0 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmissivity | 总计,3000µm | ISO 13468 | 86.0 % |
| Haze ratio | 3000µm | ISO 14782 | 2.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 12 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 160 J/m |
| 23°C,12.7mm | ASTM D256 | 140 J/m |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.08 g/cm³ | |
| 23°C | ISO 1183 | 1.08 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 18 g/10min |
| shrinkage rate | 内部方法 | 0.40-0.60 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 41.0 Mpa | |
| 屈服,23°C | ISO 527-2 | 48.0 Mpa | |
| elongation | 断裂 | ASTM D638 | 40 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 15 % |
| flexural modulus | ASTM D790 | 1810 Mpa | |
| 23°C | ISO 178 | 1870 Mpa | |
| bending strength | ASTM D790 | 63.0 Mpa | |
| 23°C | ISO 178 | 66.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.