POM DURACON® OL-10 CF2001 JAPAN POLYPLASTIC
181
- Unit Price:US$ 18,697 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High rigidity｜filling｜High temperature resistance
- Application Areas:Automotive sector
- Color:--
- Grade:Toughened grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 70 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 82.0 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | 内部方法 | 1.2E-04 cm/cm/°C |
| TD：23to55°C | 内部方法 | 1.2E-04 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ColorNumber | CF2001 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.8 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 2E+16 ohms | |
| volume resistivity | IEC 60093 | 5E+14 ohms·cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.41 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 10 g/10min |
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 9.00 cm3/10min |
| shrinkage rate | TD:2.00mm | ISO 294-4 | 1.9 % |
| MD:2.00mm | ISO 294-4 | 1.9 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.60 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2350 Mpa | |
| tensile strength | ISO 527-2 | 48.0 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 46 % | |
| flexural modulus | ISO 178 | 2200 Mpa | |
| bending strength | ISO 178 | 70.0 Mpa | |
| coefficient of friction | Dynamic2 | JISK7218 | 0.30 |
| 与钢-动态3 | JISK7218 | 0.19 | |
| Wear factor | 0.98MPa,0.30m/sec4 | JISK7218 | <1.0 10^-8mm³/N·m |
| 0.98MPa,0.30m/sec5 | JISK7218 | 40 10^-8mm³/N·m | |
| 0.060MPa,0.15m/sec6 | JISK7218 | 1200 10^-8mm³/N·m | |
| 0.060MPa,0.15m/sec7 | JISK7218 | 3000 10^-8mm³/N·m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.