ABS STAREX® NH-0825 Samsung Cheil South Korea

440

Unit Price:US$ 2,710 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:small home appliances
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	23 kJ/m²
Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	220 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	22 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75mm	UL 94	V-2
	UL flame retardant rating	1.5mm	UL 94	V-2
		UL flame retardant rating	2.5mm	UL 94	V-2
		UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-2

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/50	2300 Mpa
tensile strength	Yield	ASTM D638	41.0 Mpa
	tensile strength	Yield	ISO 527-2/50	43.0 Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	33.0 Mpa
Tensile strain	Break	ISO 527-2/50	18 %
Bending modulus		ASTM D790	2200 Mpa
Bending modulus	Bending modulus		ISO 178	2240 Mpa
bending strength		ASTM D790	65.0 Mpa
bending strength	bending strength		ISO 178	67.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	71.0 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	85.0 °C
Vicat softening temperature	--	ISO 306/B50	89.0 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	91.0 °C
Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	83.0 °C
	Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	90.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	78.0 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	200°C/5.0kg	ASTM D1238	9.0 g/10min
melt mass-flow rate	melt mass-flow rate	200°C/5.0kg	ISO 1133	9.0 g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.30-0.60 %
density		ASTM D792	1.05 g/cm³
density	density		ISO 1183	1.05 g/cm³

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	105
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	105

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.