Material Properties:Flame retardant｜High gloss｜high viscosity｜ Illuminated｜High viscosity products
Application Areas:Fiber grade
Color:--
Grade:Flame retardant grade

Technical Data Sheet Compare

physical property	Test Method	Test Result
Terminal carboxyl content	QB	56±3 MEQ/KG
Terminal amino content	QB	36±3 MEQ/KG
Water absorption rate	GB	≤700 ppm
relative viscosity	QB	3.20±0.01
Impurities and color particles	QB	≤0.017 %

other	Test Condition	Test Method	Test Result
characteristic			有光、高粘度产品
purpose			用于注塑成型挤出.还可用于不同用途的复丝挤出。作为改性基料.特别适宜于阻燃改性

Mechanical properties	Test Method	Test Result
elongation	ISO 527	30.9 %
Flexural modulus	ISO 178	0.9 GPa
Tensile modulus	ISO 527	2.4 GPa
Charpy Notched Impact Strength	ISO 179	7.9 KJ/m
tensile strength	ISO 527	78.2 Mpa
Charpy Notched Impact Strength	ISO 179	不断 KJ/m
Impact strength of cantilever beam gap	ISO 180	5.4 KJ/m
bending strength	ISO 178	73.7 Mpa

Electrical performance	Test Condition	Test Method	Test Result
dielectric strength		IEC 243	-- KV/mm
Volume resistivity		IEC 93	-- Ω.cm

Thermal performance	Test Method	Test Result
Heat distortion temperature	ISO 75	71.6 °C
melt mass-flow rate	ISO 1133	3.4 g/10min
Linear coefficient of thermal expansion	ASTM D696	7.5
melting temperature	ISO 3146	235-258 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.