PPS DURAFIDE® 6565A6 JAPAN POLYPLASTIC
208
- Unit Price:US$ 3,903 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:107MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:transparent｜High temperature resistance｜High mobility｜Flame retardant｜Glass fiber reinforced
- Application Areas:Electronic field｜Electrical field
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 95 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 275 °C |
| Linear coefficient of thermal expansion | MD | 内部方法 | 1E-05 cm/cm/°C |
| TD | 内部方法 | 3E-05 cm/cm/°C | |
| Combustibility (rate) | UL 94 | V-0 | |
| vicat | ASTM D1525/ISO R306 | 275 ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | - mm/mm.℃ |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 低温模具.良好树脂间粘接性 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ColorNumber | HF2000/HD9050 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | 1kHz | IEC 60250 | 0.013 |
| 1MHz | IEC 60250 | 5E-03 | |
| 耐电弧性 | IEC 60250 | 189 sec | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| volume resistivity | IEC 60093 | 2E+16 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 16 KV/mm |
| relative permittivity | 1kHz | IEC 60250 | 5.40 |
| 1MHz | IEC 60250 | 5.40 | |
| volume resistivity | ASTM D257/IEC 60093 | 2.0 x 10^ 16 Ω.cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt viscosity | 310°C,1000sec^-1 | ISO 11443 | 280000 mPa·s |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.010 % |
| density | ASTM D792/ISO 1183 | 1.96 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.01 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2 | 125 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.0 % |
| flexural modulus | ISO 178 | 18200 Mpa | |
| bending strength | ISO 178 | 165 Mpa | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 4.5 kg·cm/cm(J/M)ft·lb/in | |
| Elongation at break | ASTM D638/ISO 527 | 1 % | |
| tensile strength | ASTM D638/ISO 527 | 125 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 18200 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 165 kg/cm²(MPa)[Lb/in²] | |
| Elongation at break | ASTM D638/ISO 527 | 1 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.