PC LEXAN™ PK2870 SABIC INNOVATIVE US

259

Unit Price:US$ 2,317 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:enhance｜wear resistant｜high viscosity
Application Areas:chip
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Refractive index		ISO 489	1.586
transmissivity	2540μm	ASTM D1003	88.0 %
turbidity	2540μm	ASTM D1003	<0.80 %

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	50 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	70 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-30°C	ASTM D256	150 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	750 J/m
		Impact strength of cantilever beam gap	-30°C	ISO 180/1A	55 kJ/m²
			Impact strength of cantilever beam gap	23°C	ISO 180/1A	75 kJ/m²
				Impact strength of cantilever beam gap	-30°C	ASTM D4812	NoBreak
				Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D4812	NoBreak
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak
Dart impact	23°C	ASTM D3029	170 J

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield,50.0mmSpan	ASTM D790	93.0 Mpa
tensile strength	Yield	ISO 527-2/50	65.0 Mpa
	tensile strength	Break	ASTM D638	65.0 Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	70.0 Mpa
elongation	Yield	ASTM D638	7.0 %
Tensile strain	Yield	ISO 527-2/50	7.0 %
elongation	Break	ASTM D638	>70 %
Tensile strain	Break	ISO 527-2/50	>70 %
Bending modulus	50.0mmSpan	ASTM D790	2300 Mpa
Bending modulus	Bending modulus		ISO 178	2300 Mpa
bending strength		ISO 178	95.0 Mpa
Tensile modulus		ASTM D638	2350 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2350 Mpa
tensile strength	Yield	ASTM D638	62.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	--	ISO 306/B50	149 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	150 °C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40to95°C	ASTME831	7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to80°C	ISO 11359-2	7E-05 cm/cm/°C
specific heat		ASTMC351	1250 J/kg/°C
thermal conductivity		ASTMC177	0.20 W/m/K
thermal conductivity	thermal conductivity		ISO 8302	0.20 W/m/K
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	145 °C
	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	145 °C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	130 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	130 °C
Vicat softening temperature		ASTM D152510	150 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.20 g/cm³
density	density		ISO 1183	1.20 g/cm³
melt mass-flow rate	300°C/1.2kg	ASTM D1238	2.5 g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	2.00 cm3/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	300°C/2.16kg	ISO 1133	4.00 cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
Water absorption rate	Saturation,23°C	ISO 62	0.35 %
	Water absorption rate	Equilibrium,23°C	ASTM D570	0.35 %
		Water absorption rate	Equilibrium,100°C	ASTM D570	0.58 %
		Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ISO 2039-2	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top