PC LEXAN™ 121R 21051 SABIC INNOVATIVE THAILAND
190
- Unit Price:US$ 5,347 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:50MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low viscosity｜Flame retardant｜transparent
- Application Areas:Profile｜building materials
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.20 g/cm³ | |
| Specific volume | ASTM D792 | 0.835 cm³/g | |
| density | ASTM D792 | 1.19 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 18 g/10min | |
| Shrinkage rate | 内部方法 | 0.50-0.70 % | |
| Water absorption rate | ASTM D570 | 0.15 % | |
| ASTM D570 | 0.35 % | ||
| ASTM D570 | 0.58 % | ||
| Outdoor applicability | UL 746C | f2 |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 70 | |
| ASTM D785 | 118 |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ASTM D542 | 1.586 | |
| transmissivity | ASTM D1003 | 88.0 % | |
| Haze ratio | ASTM D1003 | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| Radiation board grade | YES |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | ASTM D638 | 130 % | |
| Flexural modulus | ASTM D790 | 2340 Mpa | |
| bending strength | ASTM D790 | 96.5 Mpa | |
| Taber abraser | ASTM D1044 | 10.0 mg | |
| tensile strength | ASTM D638 | 62.1 Mpa | |
| ASTM D638 | 68.9 Mpa | ||
| elongation | ASTM D638 | 7.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 12 kJ/m² | |
| ISO 179/1eA | 65 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak | |
| ISO 179/1eU | NoBreak | ||
| Impact strength of cantilever beam gap | ASTM D256 | 690 J/m | |
| ISO 180/1A | 11 kJ/m² | ||
| ISO 180/1A | 65 kJ/m² | ||
| ASTM D4812 | 3200 J/m | ||
| Suspended wall beam without notch impact strength | ISO 180/1U | NoBreak | |
| ISO 180/1U | NoBreak | ||
| Dart impact | ASTM D3763 | 62.1 J | |
| ASTM D3029 | 169 J | ||
| Impact strength of cantilever beam gap | ASTM D1822 | 546 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+17 ohms·cm | |
| Hot wire ignition (HWI) | UL 746 | PLC 2 | |
| dielectric strength | ASTM D149 | 15 KV/mm | |
| dielectric constant | ASTM D150 | 3.17 | |
| ASTM D150 | 3.17 | ||
| ASTM D150 | 2.96 | ||
| Dissipation Factor | ASTM D150 | 9E-04 | |
| ASTM D150 | 9E-04 | ||
| ASTM D150 | 0.010 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
| High arc combustion index (HAI) | UL 746 | PLC 1 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 138 °C | |
| ASTM D648 | 129 °C | ||
| vicat | ASTM D15257 | 154 °C | |
| Linear coefficient of thermal expansion | ASTME831 | 6.8E-05 cm/cm/°C | |
| specific heat | ASTMC351 | 1260 J/kg/°C | |
| thermal conductivity | ASTMC177 | 0.25 W/m/K | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI Str | UL 746 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.