PBT VALOX™  855-1001 SABIC INNOVATIVE SHANGHAI

263
  • Unit Price:US$ 3,390 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    24MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Excellent appearance｜Glass fiber reinforced
  • Application Areas:Electrical appliances｜Construction field｜Lighting applications｜Plastic bag｜Medical supplies｜Electronic field｜Electrical field
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength23°CASTM D4812350 J/m
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5 mmUL 94V-0
mechanical propertiesTest ConditionTest MethodTest Result
bending strengthBreak, 50.0 mm SpanASTM D790143 Mpa
Bending modulus50.0 mm SpanASTM D7905000 Mpa
tensile strengthBreakASTM D63895.0 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature120 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume40 to 80 %
Temperature at the rear of the barrel240 to 255 °C
Temperature in the middle of the barrel245 to 260 °C
Temperature at the front of the material cylinder250 to 265 °C
Spray nozzle temperature245 to 260 °C
Processing (melt) temperature250 to 265 °C
Mold temperature65 to 90 °C
Back pressure0.300 to 0.700 Mpa
Screw speed50 to 80 rpm
Exhaust hole depth0.025 to 0.038 mm
thermal performanceTest ConditionTest MethodTest Result
RTIUL 746125 °C
Linear coefficient of thermal expansion-40 to 40°C，FlowASTM E8314.0E-5 cm/cm/°C
Hot deformation temperature1.8 MPa, Unannealed, 6.40 mmASTM D648187 °C
Hot deformation temperature0.45 MPa, Unannealed, 6.40 mmASTM D648204 °C
RTI ImpUL 746110 °C
RTI ElecUL 746125 °C
Linear coefficient of thermal expansion60 to 138°C，FlowASTM E8316.1E-5 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rate24 hrASTM D5700.060 %
Shrinkage rateAcross FlowFlow : 3.20 to 4.60 mmInternal Method0.80 - 1.1 %
Shrinkage rateAcross FlowFlow : 1.50 to 3.20 mmInternal Method0.50 - 0.80 %
Shrinkage rateFlow : 3.20 to 4.60 mmInternal Method0.60 - 0.90 %
Shrinkage rateFlow : 1.50 to 3.20 mmInternal Method0.40 - 0.60 %
melt mass-flow rate266°C/5.0 kgASTM D123879 g/10 min
Specific volumeASTM D7920.650 cm³/g
Electrical performanceTest ConditionTest MethodTest Result
Dissipation factor100 HzASTM D1501.0E-3
Dielectric constant1 MHzASTM D1503.30
Dielectric constant100 HzASTM D1503.50
Dielectric strength3.20 mm, in AirASTM D14920 KV/mm
Dielectric strength1.60 mm, in OilASTM D14924 KV/mm
Volume resistivityASTM D2571.0E+13 ohms·cm
Dissipation factor1 MHzASTM D1500.013
Arc resistanceASTM D495PLC 6
Compared to the anti leakage trace indexUL 746PLC 3
High arc combustion indexUL 746PLC 4
High voltage arc tracing rateUL 746PLC 4
Hot wire ignitionUL 746PLC 0
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleASTM D785119
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.