POM CELCON® M25NAT CELANESE USA
202
- Unit Price:US$ 2,504 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:63.1MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:high viscosity｜wear resistant｜High sliding｜enhance
- Application Areas:Household appliances｜Household appliances｜Fitness equipment｜Automotive sector｜Electric wire｜Cable
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 166 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,未退火 | ASTM D648 | 110 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 94.0 °C | |
| melting temperature | ASTM D3418 | 165 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 190 kJ/m² |
| 23°C,局部断裂 | ISO 179/1eU | 250 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD | ASTM D955 | 2.2 % |
| TD | ASTM D955 | 1.8 % | |
| melt mass-flow rate | ASTM D1238 | 2.5 g/10min | |
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 2.20 cm3/10min |
| shrinkage rate | TD | ISO 294-4 | 1.8 % |
| MD | ISO 294-4 | 2.2 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.75 % |
| 平衡,23°C,50%RH | ISO 62 | 0.20 % | |
| DensityMelt | 内部方法 | 1.200 g/cm³ | |
| SpecificHeatCapacity of Melt | 内部方法 | 2210 J/kg/°C | |
| ThermalConductivityofMelt | 内部方法 | 0.16 W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257 | 1E+14 ohms·cm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 2460 Mpa | |
| tensile strength | 屈服,-40°C | ASTM D638 | 94.5 Mpa |
| 屈服,23°C | ASTM D638 | 60.7 Mpa | |
| Yield,71°C | ASTM D638 | 34.5 Mpa | |
| 屈服 | ISO 527-2/1A/50 | 63.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 12 % |
| Tensile creep modulus | 1hr | ISO 899-1 | 2100 Mpa |
| 1000hr | ISO 899-1 | 1100 Mpa | |
| flexural modulus | 23°C | ISO 178 | 2430 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.