PC/PTFE LNP™ LUBRICOMP™ DFL4022 SABIC INNOVATIVE US
292
- Unit Price:US$ 6,216 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:12MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Easy to form｜Easy to demould
- Application Areas:Electronic and Electrical Applications｜Lighting applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 146 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 140 °C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 5.6E-05 cm/cm/°C |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 140 °C | |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 5.6E-05 cm/cm/°C |
| 0.45MPa, Unanealed, 3.20mm | ASTM D648 | 145 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23°C | ASTM D4812 | 740 J/m | |
| ISO 180/1U | 49 kJ/m² | ||
| 23°C,EnergyatPeakLoad | ASTM D3763 | 23.2 J | |
| 23°C | ASTM D256 | 140 J/m | |
| ISO 180/1A | 13 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flow: 24 hours | 24小时 | ASTM D955 | 0.40to0.60 % |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.10 % |
| Lateral flow: 24 hours | 横向, 24小时 | ASTM D955 | 0.60to0.80 % |
| Vertical flow direction: 24 hours | 垂直方向, 24小时 | ISO 294-4 | 0.65 % |
| Flow direction: 24 hours | 流动方向, 24小时 | ISO 294-4 | 0.50 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Wear factor | Washer | ASTM D3702Modified | 166 10^-10in^5-min/ft-lb-hr |
| bending strength | ISO 178 | 118 Mpa | |
| --1 | ASTM D638 | 4140 Mpa | |
| fracture | ASTM D638 | 5.5 % | |
| yield | ASTM D638 | 71.7 Mpa | |
| ISO 527-2 | 71.0 Mpa | ||
| fracture | ASTM D638 | 67.6 Mpa | |
| coefficient of friction | 与自身-动态 | ASTM D3702Modified | 0.38 |
| yield | ASTMD638 | 3.3 % | |
| coefficient of friction | 与自身-静态 | ASTM D3702Modified | 0.44 |
| fracture | ISO 527-2 | 5.8 % | |
| ISO 527-2 | 67.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.