other	Test Condition	Test Method	Test Result	Test Unit
characteristic			pe-100黑色加炭黑2.3%
purpose			黑色管材料
Other performance	Test Condition	Test Method	Test Result	Test Unit
Carbon black content		ISO 6964	2.25	%
Tensile modulus		ISO 527-2	900	Mpa
Oxidation induction time (OIT)	210℃	EN 728	＞20	min
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190℃/5.0kg	ISO 1133	0.22	g/10min
melt mass-flow rate	melt mass-flow rate	190℃/21.6kg	ISO 1133	6.4	g/10min
density		ISO 1183	0.959
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield	ISO 527-2	23	Mpa
Impact strength of cantilever beam gap	23℃	ISO 179	26	KJ/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30℃	ISO 179	13	KJ/m
Shore hardness		ISO 868	63
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ISO 306	74	°C
Melting temperature		DIN 53765	124-128	°C
Hot deformation temperature	HDT	ASTM D648/ISO 75	85	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	0.959
melt mass-flow rate		ASTM D1238/ISO 1133	0.23	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.