ABS HU650 KUMHO KOREA

561

Unit Price:US$ 2,760 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
95MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:heat-resisting｜High rigidity｜Low gloss｜UV resistance｜High toughness｜Moderate heat resistance
Application Areas:Engine hood parts｜Automotive External Parts｜Automotive sector｜Application in the automotive field｜Parts under the hood of a car
Color:--
Grade:Heat resistant grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	18	kJ/m²
	Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	180	J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	200	J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	19	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	--	ISO 178	70.0	Mpa
Bending modulus	--	ISO 178	2350	Mpa
Bending modulus	Bending modulus	--	ASTM D790	2210	Mpa
elongation	Break	ISO 527-2	20	%
elongation	elongation	Yield	ASTM D638	15	%
tensile strength	Yield	ISO 527-2	46.0	Mpa
tensile strength	tensile strength	Yield	ASTM D638	47.6	Mpa
bending strength	Yield	ASTM D790	67.7	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ISO 306/B50	114	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	99.0	°C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	104	°C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	112	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220°C/10.0kg	ISO 1133	5.0	g/10min
	melt mass-flow rate	220°C/10.0kg	ASTM D1238	4.0	g/10min
	melt mass-flow rate	melt mass-flow rate	200°C/21.6kg	ASTM D1238	6.0	g/10min
density		ASTMD792	1.04	g/cm³
Shrinkage rate	--	ISO 294-4	0.50-0.80	%
Shrinkage rate	Shrinkage rate	MD	ASTM D955	0.50-0.80	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale	ISO 2039-2	108
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	108

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top