PC LUPOY® 1201 10P LG CHEM KOREA
1306
- Unit Price:US$ 1,966 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:123.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:transparent｜wear resistant｜Low viscosity
- Application Areas:Toy｜Food containers｜chip｜bottle
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M 级 | ASTM D785 | 73 |
| R 级 | ASTM D785 | 118 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 退火, 4.00 mm | ASTM D648 | 144 °C |
| 1.8 MPa, 未退火, 4.00 mm | ASTM D648 | 128 °C | |
| 1.8 MPa, 退火, 4.00 mm | ASTM D648 | 141 °C | |
| vicat | ASTM D15256 | 149 °C | |
| Ball pressure temperature | IEC 60598-1 | > 125 °C | |
| Linear coefficient of thermal expansion | -40 到 82°C，流动 | ASTM D696 | 6.8E-5 cm/cm/°C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ASTM D542 | 1.586 | |
| transmissivity | ASTM D1003 | 89.0 % | |
| Haze ratio | ASTM D1003 | 0.70 to 1.5 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot filament ignition temperature | 2.0 mm | IEC 60695-2-13 | 850 °C |
| Limiting Oxygen Index | ASTM D2863 | 26 % | |
| Average degree of combustion | ASTM D746 | 3 CM |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | 无断裂 |
| Dart impact | 23°C, 3.20 mm, Total Energy | ASTM D3763 | 87.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 10 g/10 min |
| shrinkage rate | Flow | ASTM D955 | 0.50 - 0.70 % |
| Water absorption rate | 24 hr, 23°C | ASTM D570 | 0.15 % |
| 平衡, 23°C, 50% RH | ASTM D570 | 0.32 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | 23°C | ASTM D257 | 2.0E+17 ohms·cm |
| dielectric strength | ASTM D149 | 17 KV/mm | |
| dielectric constant | 60 Hz | ASTM D150 | 3.00 |
| Dissipation Factor | 60 Hz | ASTM D150 | 1.0E-3 |
| Compared to the Leakage Tracking Index (CTI) | 2.00 mm | IEC 60112 | PLC 2 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2410 Mpa | |
| tensile strength | 屈服, 23°C2 | ASTM D638 | 60.0 Mpa |
| 断裂 | ASTM D638 | 71.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 6.0 % |
| 断裂 | ASTM D638 | 150 % | |
| flexural modulus | ASTM D790 | 2410 Mpa | |
| bending strength | ASTM D790 | 96.0 Mpa | |
| Wear resistance - Change in Haze | ASTM D1004 | 45 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.