PC/ABS INFINO® NE-1030 K21441 Samsung Cheil South Korea

335

Unit Price:US$ 4,410 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:Tool handle｜TV
Color:--
Grade:Flame retardant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	17	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	16	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.0mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ASTM D790	87.0	Mpa
Bending modulus		ISO 178	2500	Mpa
Bending modulus	Bending modulus		ASTM D790	2500	Mpa
Tensile strain	Break	ISO 527-2/50	35	%
elongation	Break	ASTM D638	59	%
tensile strength	Break	ISO 527-2/50	46.0	Mpa
	tensile strength	Break	ASTM D638	54.0	Mpa
		tensile strength	Yield	ISO 527-2/50	60.0	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	63.0	Mpa
Tensile modulus		ISO 527-2/50	2500	Mpa
Tensile modulus	Tensile modulus		ASTM D638	2600	Mpa
bending strength		ISO 178	90.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	85.0	°C
	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	77.0	°C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	83.0	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	93.0	°C
Vicat softening temperature	--	ISO 306/B120	95.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	93.0	°C
Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	90.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD：3.20mm	ASTM D955	0.33-0.40	%
Shrinkage rate	Shrinkage rate	MD：3.20mm	ASTM D955	0.32-0.39	%
melt mass-flow rate	220°C/10.0kg	ISO 1133	53	g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ASTM D1238	53	g/10min
Shrinkage rate	MD:3.20mm	ISO 2577	0.32-0.39	%
Shrinkage rate	Shrinkage rate	TD:3.20mm	ISO 2577	0.33-0.40	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ISO 2039-2	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC/ABS INFINO® NE-1030 K21441 Samsung Cheil South Korea

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index