PC/ABS INFINO® NH-1001T Samsung Cheil South Korea

442

Unit Price:US$ 23,653 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
12MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:OA device
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	55	kJ/m²
	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	520	J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	640	J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	60	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	2.0mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/50	2300	Mpa
tensile strength	Yield	ASTM D638	57.0	Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	55.0	Mpa
Tensile modulus		ASTM D638	2300	Mpa
bending strength		ISO 178	83.0	Mpa
bending strength	bending strength		ASTM D790	78.0	Mpa
Bending modulus		ISO 178	2300	Mpa
Bending modulus	Bending modulus		ASTM D790	2200	Mpa
Tensile strain	Break	ISO 527-2/50	99	%
elongation	Break	ASTM D638	87	%
tensile strength	Break	ASTM D638	52.0	Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	52.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/B120	95.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	93.0	°C
Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	77.0	°C
	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	84.0	°C
		Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	88.0	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	90.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220°C/10.0kg	ISO 1133	25	g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ASTM D1238	25	g/10min
density		ISO 1183	1.16	g/cm³
density	density		ASTM D792	1.16	g/cm³
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ISO 2039-2	114
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	114

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC/ABS INFINO® NH-1001T Samsung Cheil South Korea

Material Description

Material Certification

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index